Ultra-high-performance concrete (UHPC) is a new type of high-performance cement-based composite. It is widely used in important buildings, bridges, national defense construction, etc. because of its excellent mechanical properties and durability. Freeze thaw and salt erosion damage are one of the main causes of concrete structure failure. The use of UHPC prepared with multi-walled carbon nanotubes (MWCNTs) is an effective method to enhance the durability of concrete structures in complex environments. In this work, the optimal mix proportion based on mechanical properties was obtained by changing the content of MWCNTs and water binder ratio to prepare MWCNTs UHPC. Then, based on the changes in the compressive strength, mass loss rate, and relative dynamic modulus of elasticity (RDME), the damage degree of concrete under different salt erosion during 1500 freeze-thaw (FT) cycles was analyzed. The changes in the micro pore structure were characterized by scanning electron microscope (SEM) and nuclear magnetic resonance (NMR). The test results showed that the optimum mix proportion at the water binder ratio was 0.19 and 0.1% MWCNTs. At this time, the compressive strength was 34.1% higher and the flexural strength was 13.6% higher than when the MWCNTs content was 0. After 1500 salt freezing cycles, the appearance and mass loss of MWCNTs-UHPC prepared according to the best ratio changed little, and the maximum mass loss was 3.18%. The higher the mass fraction of the erosion solution is, the lower the compressive strength and RDME of concrete after FT cycles. The SEM test showed that cracks appeared in the internal structure and gradually increased due to salt freezing damage. However, the microstructure of the concrete was still relatively dense after 1500 salt freezing cycles. The NMR test showed that the salt freezing cycle has a significant influence on the change in the small pores, and the larger the mass fraction of the erosion solution, the smaller the change in the proportion of pores. After 1500 salt freezing cycles, the samples did not fail, which shows that MWCNTs UHPC with a design service life of 150 years has good salt freezing resistance under the coupling effect of salt corrosion and the FT cycle.

Carbon nanotubes are considered as a promising material for the development of high performance concrete. In order to study the effects of Multi walled carbon nanotubes (MWCNTs) content, water cement ratio and addition method on the mechanical properties and microstructure of cement-based composites, specimens with MWCNTs content of 0%, 0.05%, 0.08%, 0.10%, 0.15%, 0.20%, and 0.30% were prepared when the water cement ratio was 0.25, 0.3, 0.35, and 0.4, respectively. The physical properties, mechanical properties and microstructure were tested. The test results show that with the increase of MWCNTs content, the flexural strength and compressive strength of cement-based composites increase first and then decrease. The DIC test shows that the displacement and strain of the specimen with MWCNTs are smaller than the blank sample under the same concentrated load, while it is opposite before the failure of sample. The SEM test shows that MWCNTs play the role of bridging and filling in the matrix. The EDS analysis results show that the five main elements of carbon, oxygen, aluminum, silicon, and calcium in the composite are evenly distributed in the cement matrix.

Few studies have been published on the dynamic centrifuge model test of cohesive soil under earthquake action. The seismic response of cohesive soil foundation and tunnel was studied by the centrifuge experiment and numerical modelling. Through a comparison of the acceleration results of tunnel and cohesive soil foundation and the pore pressure and displacement of cohesive soil foundation, the influence of tunnel on cohesive soil foundation is discussed. The weak position of the tunnel under earthquake is predicted by effective numerical modelling. The results show that: (1) Under the Parkfield seismic wave, the natural frequency of the cohesive soil foundation with the tunnel is about 0.3 Hz, which is the most clear for the amplification of the low frequency component and the amplification of the seismic acceleration from bottom to top; (2) The acceleration response of the tunnel itself is small, and the effect of seismic wave on the surrounding soil is weakened due to the existence of tunnels; (3) The maximum bending moment and shear force appear at the corner of the rectangular tunnel, and the maximum axial force appears at the top of the rectangular tunnel; (4) The lateral displacement of the surface soil is the largest, and the pore pressure reduction in the middle soil is the largest compared with other soil layers. The existence of tunnels weakens the liquefaction potential of the surrounding soil.

In this paper, the feasibility of multi-walled carbon nanotube (MWCNT)-modified clay as a landfill liner material is investigated. Experiments were conducted on the modified clay with 0.5%, 1%, and 2% MWCNTs. The effects of the MWCNTs on the compaction characteristics, permeability coefficient, stress–strain curve, peak deviation stress, shear strength parameters (internal friction angle and cohesion), microstructures, and adsorption performance of the clay were analyzed. The results showed that the optimum moisture content (OMC) increased from 16.15% to 18.89%, and the maximum dry density (MDD) decreased from 1.79 g/cm³ to 1.72 g/cm³ with the increase in MWCNTs. The permeability coefficients firstly fell and then gradually rose as the MWCNTs increased; the minimum permeability coefficient was 8.62 × 10⁻⁹ cm/s. The MWCNTs can also effectively increase the peak deviation stress of the clay, and at the maximum level, the peak deviation stress was increased by 286%. SEM images were processed using the Pore and Crack Analysis System (PCAS), and the results showed that the appropriate amount of MWCNTs could fill the pores and strengthen the clay structure. The effect of the MWCNT-modified clay on the adsorption performance of common heavy metal ions Cd²⁺, Mn²⁺ and Cu²⁺ in landfill leachate was analyzed by batch adsorption tests. The maximum adsorption capacities (Q_max) of Cu²⁺, Cd²⁺ and Mn²⁺ in the 2% MWCNT-modified clay were, respectively, 41.67 mg/g, 18.69 mg/g, and 4.97 mg/g. Compared with the clay samples without MWCNTs, the adsorption properties of Cu²⁺, Cd²⁺, and Mn²⁺ were increased by 228%, 124%, and 202%, respectively. Overall, the results suggest that MWCNT-modified clays have the potential to be suitable barrier materials for the construction of landfills.

There is a huge risk of dam failure during the operation of tailings ponds. Domestic and foreign scholars have conducted extensive research on the assessment and prevention of dam failure risks during the operation of tailings ponds, but there are still many shortcomings. On the basis of exploring the key issues of dam failure risk assessment during the operation of tailings dams, this paper establishes a comprehensive evaluation index system for dam failure risk during the operation of tailings dams based on ten principles including scientificity, systematicity, and operability. By exploring the use of the change statistical mapping method, we can determine the weight of indicators. A risk assessment model was constructed using the fuzzy comprehensive evaluation method; compared to the traditional fuzzy comprehensive evaluation method, this model determines weights in a more extensive and scientific manner. The scientific and effective nature of the model was verified through case analysis of the Shouyun Iron Mine and Shangyu Tailings Reservoir in Beijing. Finally, in response to the risk of dam failure during the operation of tailings ponds, scientific prevention and control measures were proposed from four aspects: personnel risk prevention and control, inherent risk prevention and control of tailings ponds, environmental factor risk prevention and control, and management risk prevention and control.

The use of iron tailing powder (ITP) and granulated blast-furnace slag (GBFS) offers a feasible route for preparing low-cement mortar while recycling industrial by-products. In this study, seven cement mortar mixtures were designed to investigate the influence of the ITP–GBFS ratio on mechanical properties, microstructure, hydration products, and chloride ion penetration resistance. The mixtures included plain cement mortar (A0), mortar with 50% ITP (A1), mortar with 50% GBFS (A2), and four composite mixtures (A3–A6) in which ITP and GBFS jointly replaced 50% of cement at different ratios. The results showed that the mixture containing 20% ITP and 30% GBFS (A4) exhibited the best overall performance among the composite mixtures. At 28 d, A4 reached a compressive strength of 51.3 MPa and a flexural strength of 11.0 MPa, exceeding those of the plain cement control. SEM and XRD analyses suggested that the optimized ITP–GBFS combination promoted the formation of poorly crystalline hydration products, such as C–S–H/C–A–S–H gels, and refined the pore structure, resulting in a denser hardened matrix. The rapid chloride migration test showed that the chloride migration coefficient of A4 was 15.47 × 10⁻¹² m²/s, only slightly higher than that of A0, indicating that the optimized composite binder maintained chloride penetration resistance close to that of plain cement mortar while replacing 50% of cement. The results indicate that a properly proportioned ITP–GBFS binder can maintain acceptable strength and chloride resistance while reducing cement consumption.