Development of cost-effective oxygen evolution catalysts is of capital importance for the deployment of large-scale energy-storage systems based on metal–air batteries and reversible fuel cells. In this direction, a wide range of materials have been explored, especially under more favorable alkaline conditions, and several metal chalcogenides have particularly demonstrated excellent performances. However, chalcogenides are thermodynamically less stable than the corresponding oxides and hydroxides under oxidizing potentials in alkaline media. Although this instability in some cases has prevented the application of chalcogenides as oxygen evolution catalysts and it has been disregarded in some others, we propose to use it in our favor to produce high-performance oxygen evolution catalysts. We characterize here the in situ chemical, structural, and morphological transformation during the oxygen evolution reaction (OER) in alkaline media of Cu₂S into CuO nanowires, mediating the intermediate formation of Cu(OH)₂. We also test their OER activity and stability under OER operation in alkaline media and compare them with the OER performance of Cu(OH)₂ and CuO nanostructures directly grown on the surface of a copper mesh. We demonstrate here that CuO produced from in situ electrochemical oxidation of Cu₂S displays an extraordinary electrocatalytic performance toward OER, well above that of CuO and Cu(OH)₂ synthesized without this transformation.

Urchin‐shaped NiCo₂Se₄ (u‐NCSe) nanostructures as efficient sulfur hosts are synthesized to overcome the limitations of lithium–sulfur batteries (LSBs). u‐NCSe provides a beneficial hollow structure to relieve volumetric expansion, a superior electrical conductivity to improve electron transfer, a high polarity to promote absorption of lithium polysulfides (LiPS), and outstanding electrocatalytic activity to accelerate LiPS conversion kinetics. Owing to these excellent qualities as cathode for LSBs, S@u‐NCSe delivers outstanding initial capacities up to 1403 mAh g⁻¹ at 0.1 C and retains 626 mAh g⁻¹ at 5 C with exceptional rate performance. More significantly, a very low capacity decay rate of only 0.016% per cycle is obtained after 2000 cycles at 3 C. Even at high sulfur loading (3.2 mg cm⁻²), a reversible capacity of 557 mAh g⁻¹ is delivered after 600 cycles at 1 C. Density functional theory calculations further confirm the strong interaction between NCSe and LiPS, and cytotoxicity measurements prove the biocompatibility of NCSe. This work not only demonstrates that transition metal selenides can be promising candidates as sulfur host materials, but also provides a strategy for the rational design and the development of LSBs with long‐life and high‐rate electrochemical performance.

There is an urgent need for cost‐effective strategies to produce hydrogen from renewable net‐zero carbon sources using renewable energies. In this context, the electrochemical hydrogen evolution reaction can be boosted by replacing the oxygen evolution reaction with the oxidation of small organic molecules, such as ethylene glycol (EG). EG is a particularly interesting organic liquid with two hydroxyl groups that can be transformed into a variety of C1 and C2 chemicals, depending on the catalyst and reaction conditions. Here, a catalyst is demonstrated for the selective EG oxidation reaction (EGOR) to formate on nickel selenide. The catalyst nanoparticle (NP) morphology and crystallographic phase are tuned to maximize its performance. The optimized NiS electrocatalyst requires just 1.395 V to drive a current density of 50 mA cm⁻² in 1 m potassium hydroxide (KOH) and 1 m EG. A combination of in situ electrochemical infrared absorption spectroscopy (IRAS) to monitor the electrocatalytic process and ex situ analysis of the electrolyte composition shows the main EGOR product is formate, with a Faradaic efficiency above 80%. Additionally, C2 chemicals such as glycolate and oxalate are detected and quantified as minor products. Density functional theory (DFT) calculations of the reaction process show the glycol‐to‐oxalate pathway to be favored via the glycolate formation, where the CC bond is broken and further electro‐oxidized to formate.