P2/O3 composite sodium layered oxide has emerged as a promising cathode for high-performance Na-ion batteries. However, it has been challenging to regulate accurately the phase ratio of P2/O3 composite due to their high compositional diversity, which brings about some difficulty in manipulating the electrochemical performance of P2/O3 composite. Here, we explore the effect of Ti substitution and the synthesis temperature on the crystal structure and Na storage performance of Na_0.8Ni_0.4Mn_0.6O₂. The investigation indicates Ti-substitution and altering synthesis temperature can rationally manipulate the phase ratio of P2/O3 composite, thereby purposefully regulating the cycling and rate performance of P2/O3 composite. Typically, O3-rich Na_0.8Ni_0.4Mn_0.4Ti_0.2O₂-950 shows excellent cycling stability with a capacity retention of 84% (3C, 700 cycles). By elevating the proportion of P2 phase, Na_0.8Ni_0.4Mn_0.4Ti_0.2O₂-850 displays concurrently improved rate capability (65% capacity retention at 5 C) and comparable cycling stability. These findings will help guide the rational design of high-performance P2/O3 composite cathodes for sodium-ion batteries.

Hard carbons as promising anode materials for Na-ion batteries (NIBs) have captured extensive attention because of their low operation voltage, easy synthesis process, and competitive specific capacity. However, there are still several disadvantages, such as high cost and low initial coulombic efficiency, which limit their large-scale commercial applications. Herein, pine nut shells (PNSs), a low-cost biomass waste, are used as precursors to prepare hard carbon materials. Via a series of washing and heat treatment procedures, a pine nut shell hard carbon (PNSHC)-1400 sample has been obtained and delivers a reversible capacity of around 300 mAh/g, a high initial coulombic efficiency of 84%, and good cycling performance. These excellent Na storage properties indicate that PNSHC is one of the most promising candidates of hard carbon anodes for NIBs.