The linear dynamic viscoelastic properties and non-linear transient rheology of sodium carboxymethylcellulose solutions (Na-CMC) in propylene glycol/water mixtures were investigated. Measurements were carried out for the solutions of Na-CMC with three different degrees of substitution (DS), namely 0.62, 0.79, 1.04, and the similar average molecular weight (M_w ≈ 250,000 g/mol). The strong synergism between the molecules of Na-CMC with DS of 0.62 and 0.79, and propylene glycol has been observed. The occurrence of the overshoot shear stress and the low loss tangent values indicate the physical cross-linking of the polymer chains. The increase of propylene glycol concentration over 80 wt% and sodium carboxymethylcellulose (DS = 0.7) over 1.6 wt% leads to the formation of a physical cross-link network. The absence of overshoot shear stress and terminal behaviour in SAOS flow of the Na-CMC_1.04 solutions in the PG/water mixture shows that no intermolecular cross-linking of polymer chains occurred in them.

The aim of the research presented in this paper was to determine the effect of dihydroxy alcohols on the rheological properties of sodium carboxymethylcellulose (Na-CMC) solutions with different degrees of substitution and different average molecular masses. Rheological measurements were carried out with a rotational rheometer in continuous and oscillatory flows. Two dihydroxy alcohols were used in the study: butane-1,3-diol and propane-1,2-diol. The concentration of Na-CMC in the solutions was 1.6% and 2.2%, while the concentration of the dihydroxy alcohols ranged from 10% to 60%. The measurements show that the viscoelastic properties of Na-CMC solutions are strongly linked to the type of solvent used. The application of low-substituted high-molecular-mass Na-CMC makes it possible to obtain fluids with the properties of weak physical gels. On the other hand, the dissolution of Na-CMC with a high degree of substitution (>1) and low molecular mass in dihydroxy alcohol/water mixtures yields a viscoelastic fluid. Based on oscillatory measurements, increasing concentrations of polyhydroxy alcohols in Na-CMC solutions were found to induce an increase in the strength of the network structure. At the same concentrations of polyhydroxy alcohols in solutions containing butane-1,3-diol, a stronger network structure is formed compared to solutions containing propane-1,2-diol. The rheological measurement results presented in this paper may be useful in the formulation of drug carriers and cosmetics in which rheological properties are a significant factor.