The aim of the research presented in this paper was to determine the effect of dihydroxy alcohols on the rheological properties of sodium carboxymethylcellulose (Na-CMC) solutions with different degrees of substitution and different average molecular masses. Rheological measurements were carried out with a rotational rheometer in continuous and oscillatory flows. Two dihydroxy alcohols were used in the study: butane-1,3-diol and propane-1,2-diol. The concentration of Na-CMC in the solutions was 1.6% and 2.2%, while the concentration of the dihydroxy alcohols ranged from 10% to 60%. The measurements show that the viscoelastic properties of Na-CMC solutions are strongly linked to the type of solvent used. The application of low-substituted high-molecular-mass Na-CMC makes it possible to obtain fluids with the properties of weak physical gels. On the other hand, the dissolution of Na-CMC with a high degree of substitution (>1) and low molecular mass in dihydroxy alcohol/water mixtures yields a viscoelastic fluid. Based on oscillatory measurements, increasing concentrations of polyhydroxy alcohols in Na-CMC solutions were found to induce an increase in the strength of the network structure. At the same concentrations of polyhydroxy alcohols in solutions containing butane-1,3-diol, a stronger network structure is formed compared to solutions containing propane-1,2-diol. The rheological measurement results presented in this paper may be useful in the formulation of drug carriers and cosmetics in which rheological properties are a significant factor.

The study presents results of rheological tests and measurements of pressure drops occurring during the flow of aqueous solutions of a mixture of drag reducing surfactants: cocamidopropyl betaine (CAPB, zwitterionic surfactant) and cocamide DEA (nonionic surfactant) through straight pipes. Tests were carried out at different CAPB/DEA weight ratios and different total concentrations of surfactants in the solution. Rheological measurements demonstrate the formation of a shear-induced structure (SIS) in the temperature range below 10 °C, which provides evidence for the presence of wormlike micelles in CAPB/DEA solutions. Drag reduction was observed during the flow of CAPB/DEA solutions in the temperature range from 3 to 45 °C, however, above 25 °C the degree of drag reduction was markedly decreased. The lower temperature limit at which drag reduction occurs depends on the CAPB and DEA weight ratio in the solution. In the range of higher temperatures, during the flow of CAPB/DEA solutions (similarly to flexible-chain polymer solutions) the onset of drag reduction is noted above a certain critical value of the Re_c,0 number, whose value depends on the temperature of the solution, diameter of the pipe and the weight ratio of surfactants. At the same time, the critical value of wall shear stress τ_w,c0 corresponding to the critical value of Re_c,0 is approximately independent of pipe diameter. The critical value of the Re_c,0 number has been linked to the clouding of CAPB/DEA solutions.