The quadridentate N-heterocyclic ligand 6-(5,5,8,8-tetramethyl-5,6,7,8-tetrahydro-1,2,4-benzotriazin-3-yl)-2,2′ : 6′,2′′-terpyridine (CyMe₄-hemi-BTBP) has been synthesized and its interactions with Am(III), U(VI), Ln(III) and some transition metal cations have been evaluated by X-ray crystallographic analysis, Am(III)/Eu(III) solvent extraction experiments, UV absorption spectrophotometry, NMR studies and ESI-MS. Structures of 1 : 1 complexes with Eu(III), Ce(III) and the linear uranyl (UO₂ ²⁺) ion were obtained by X-ray crystallographic analysis, and they showed similar coordination behavior to related BTBP complexes. In methanol, the stability constants of the Ln(III) complexes are slightly lower than those of the analogous quadridentate bis-triazine BTBP ligands, while the stability constant for the Yb(III) complex is higher. ¹H NMR titrations and ESI-MS with lanthanide nitrates showed that the ligand forms only 1 : 1 complexes with Eu(III), Ce(III) and Yb(III), while both 1 : 1 and 1 : 2 complexes were formed with La(III) and Y(III) in acetonitrile. A mixture of isomeric chiral 2 : 2 helical complexes was formed with Cu(I), with a slight preference (1.4 : 1) for a single directional isomer. In contrast, a 1 : 1 complex was observed with the larger Ag(I) ion. The ligand was unable to extract Am(III) or Eu(III) from nitric acid solutions into 1-octanol, except in the presence of a synergist at low acidity. The results show that the presence of two outer 1,2,4-triazine rings is required for the efficient extraction and separation of An(III) from Ln(III) by quadridentate N-donor ligands.

In this paper, aluminum-doped zinc oxide (ZnO:Al or AZO) thin films are grown using atomic layer deposition (ALD) and the influence of postdeposition UV–ozone and thermal annealing treatments on the films’ properties are investigated. X-ray diffraction (XRD) revealed a polycrystalline wurtzite structure with a preferable (100) orientation. The crystal size increase after the thermal annealing is observed while UV–ozone exposure led to no significant change in crystallinity. The results of the X-ray photoelectron spectroscopy (XPS) analyses show that a higher amount of oxygen vacancies exists in the ZnO:Al after UV–ozone treatment, and that the ZnO:Al, after annealing, has a lower amount of oxygen vacancies. Important and practical applications of ZnO:Al (such as transparent conductive oxide layer) were found, and its electrical and optical properties demonstrate high tunability after postdeposition treatment, particularly after UV–Ozone exposure, offers a noninvasive and easy way to lower the sheet resistance values. At the same time, UV–Ozone treatment did not cause any significant changes to the polycrystalline structure, surface morphology, or optical properties of the AZO films.