Based on molecular dynamics (MD), in this study, a model was established to simulate the initial coating morphology of silver paste by using a random algorithm, and the effects of different sizes of particles on sintering porosity were also analyzed. The MD result reveals that compared with the sintering process using large-scale silver particles, the sintering process using multi-scale silver particles would enhance the densification under the same sintering conditions, which authenticates the feasibility of adding small silver particles to large-scale silver particles in theory. In addition, to further verify the feasibility of the multi-scale sintering, a semi in-situ observation was prepared for a sintering experiment using micro-nano multi-scale silver paste. The feasibility of multi-scale silver sintering is proved by theoretical and experimental means, which can provide a meaningful reference for optimizing the sintering process and the preparation of silver paste for die-attach in powering electronics industry. In addition, it is hoped that better progress can be made on this basis in the future.

This study proposes a low-temperature transient liquid phase bonding (TLPB) method using Sn58Bi/porous Cu/Sn58Bi to enable efficient power-device packaging at high temperatures. The bonding mechanism is attributed to the rapid reaction between porous Cu and Sn58Bi solder, leading to the formation of intermetallic compounds with high melting point at low temperatures. The present paper investigates the effects of bonding atmosphere, bonding time, and external pressure on the shear strength of metal joints. Under formic acid (FA) atmosphere, Cu₆Sn₅ forms at the porous Cu foil/Sn58Bi interface, and some of it transforms into Cu₃Sn. External pressure significantly reduces the micropores and thickness of the joint interconnection layer, resulting in a ductile fracture failure mode. The metal joint obtained under a pressure of 10 MPa at 250 °C for 5 min exhibits outstanding bonding mechanical performance with a shear strength of 62.2 MPa.