This work presents the design and application of a low-cycle reciprocating loading test on 23 recycled aggregate concrete-filled steel tube columns and 3 ordinary concrete-filled steel tube columns. Additionally, a systematic study on the influence of various parameters (e.g., slenderness ratio, axial compression ratio, etc.) was conducted on the seismic performance of the specimens. The results show that all the specimens have good hysteresis performance and a similar development trend of skeleton curve. The influence of slenderness ratio on the seismic index of the specimens is more significant than that of the axial compression ratio and the steel pipe wall thickness. Furthermore, artificial intelligence was applied to estimate the influence of parameter variation on the seismic performance of concrete columns. Specifically, Random Forest with hyperparameters tuned by Firefly Algorithm was chosen. The high correlation coefficients (R) and low root mean square error values from the prediction results showed acceptable accuracy. In addition, sensitivity analysis was applied to rank the influence of the aforementioned input variables on the seismic performance of the specimens. The research results can provide experimental reference for the application of steel tube recycled concrete in earthquake areas.

Waste glass (WG) is unsustainable due to its nonbiodegradable property. However, its main ingredient is silicon dioxide, which can be utilised as a supplementary cementitious material. Before reusing WG, the flexural strength (FS) and alkali–silica reaction (ASR) expansion of WG concrete are two essential properties that must be investigated. This study produced mortar containing activated glass powder using mechanical, chemical, and mechanical–chemical (combined) approaches. The results showed that mortar containing 30% WG powder using the combined method was optimal for improving the FS and mitigating the ASR expansion. The microstructure analysis was implemented to explore the activation effect on the glass powder and mortar. Moreover, a random forest (RF) model was proposed with hyperparameters tuned by beetle antennae search (BAS), aiming at predicting FS and ASR expansion precisely. A large database was established from the experimental results based on 549 samples prepared for the FS test and 183 samples produced for the expansion test. The BAS-RF model presented high correlation coefficients for both FS (0.9545) and ASR (0.9416) data sets, showing much higher accuracy than multiple linear regression and logistic regression. Finally, a sensitivity analysis was conducted to rank the variables based on importance. Apart from the curing time, the particle granularity and content of WG were demonstrated to be the most sensitive variable for FS and expansion, respectively.

High-strength concrete (HSC) is a functional material possessing superior mechanical performance and considerable durability, which has been widely used in long-span bridges and high-rise buildings. Unconfined compressive strength (UCS) is one of the most crucial parameters for evaluating HSC performance. Previously, the mix design of HSC is based on the laboratory test results which is time and money consuming. Nowadays, the UCS can be predicted based on the existing database to guide the mix design with the development of machine learning (ML) such as back-propagation neural network (BPNN). However, the BPNN’s hyperparameters (the number of hidden layers, the number of neurons in each layer), which is commonly adjusted by the traditional trial and error method, usually influence the prediction accuracy. Therefore, in this study, BPNN is utilised to predict the UCS of HSC with the hyperparameters tuned by a bio-inspired beetle antennae search (BAS) algorithm. The database is established based on the results of 324 HSC samples from previous literature. The established BAS-BPNN model possesses excellent prediction reliability and accuracy as shown in the high correlation coefficient (R = 0.9893) and low Root-mean-square error (RMSE = 1.5158 MPa). By introducing the BAS algorithm, the prediction process can be totally automatical since the optimal hyperparameters of BPNN are obtained automatically. The established BPNN model has the benefit of being applied in practice to support the HSC mix design. In addition, sensitivity analysis is conducted to investigate the significance of input variables. Cement content is proved to influence the UCS most significantly while superplasticizer content has the least significance. However, owing to the dataset limitation and limited performance of ML models which affect the UCS prediction accuracy, further data collection and model update must be implemented.

Construction and demolition (C&D) waste has become a research hotspot due to the need for environmental sustainability and strength enhancement of cementitious materials. However, wider applications of C&D waste are limited, as its non-homogeneous surface nature limits its workability. This research evaluated the feasible utilization of C&D waste as aggregates in polypropylene-fiber-reinforced cement-stabilized soil (CSS) under sulfate-alkali activation. CSS specimens incorporated Portland cement and C&D waste in 10%, 20%, and 30% proportions. Also, polypropylene fiber after alkali activation by sodium sulfate (at 0.2%, 0.4%, and 0.8% dosing level) was defined as 1%, 2%, and 4%. Strength enhancement was examined through unconfined compressive strength (UCS) and flexural strength tests at 7, 14 and 28 days. Test results indicated that mechanical properties showed significant improvement with increasing levels of Portland cement and sodium sulfate, while the improvement dropped after excessive addition of C&D waste and polypropylene fiber. Optimal proportioning was determined as 30%, 4%, 20%, and 0.8% for Portland cement, polypropylene fiber, C&D waste, and sodium sulfate, respectively. Scanning electron microscope (SEM) analysis attributed the enhancement to hydration product (ettringite) formation, bridging effect and increased particle friction. Additionally, the decrease in amplification was ascribed to the destruction of interface transition-zone (ITZ) strength, resulting in premature failure.

Cement stabilized soil (CSS) yields wide application as a routine cementitious material due to cost-effectiveness. However, the mechanical strength of CSS impedes development. This research assesses the feasible combined enhancement of unconfined compressive strength (UCS) and flexural strength (FS) of construction and demolition (C&D) waste, polypropylene fiber, and sodium sulfate. Moreover, machine learning (ML) techniques including Back Propagation Neural Network (BPNN) and Random Forest (FR) were applied to estimate UCS and FS based on the comprehensive dataset. The laboratory tests were conducted at 7-, 14-, and 28-day curing age, indicating the positive effect of cement, C&D waste, and sodium sulfate. The improvement caused by polypropylene fiber on FS was also evaluated from the 81 experimental results. In addition, the beetle antennae search (BAS) approach and 10-fold cross-validation were employed to automatically tune the hyperparameters, avoiding tedious effort. The consequent correlation coefficients (R) ranged from 0.9295 to 0.9717 for BPNN, and 0.9262 to 0.9877 for RF, respectively, indicating the accuracy and reliability of the prediction. K-Nearest Neighbor (KNN), logistic regression (LR), and multiple linear regression (MLR) were conducted to validate the BPNN and RF algorithms. Furthermore, box and Taylor diagrams proved the BAS-BPNN and BAS-RF as the best-performed model for UCS and FS prediction, respectively. The optimal mixture design was proposed as 30% cement, 20% C&D waste, 4% fiber, and 0.8% sodium sulfate based on the importance score for each variable.