Nanoparticles (NPs) have attracted great interest in various fields owing to their antimicrobial activity; however, the use of NPs as fungicides on plants has not been sufficiently investigated. In this study, the antifungal activities of sulfur nanoparticles (S-NPs) and copper nanoparticles (Cu-NPs) prepared by a green method were evaluated against Botrytis cinerea and Sclerotinia sclerotiorum. The formation of NPs was confirmed by transmission electron microscopy (TEM) and X-ray diffraction analysis (XRD). The antifungal activities of NPs (5–100 µg/mL), CuSO₄ (4000 µg/mL), and micro sulfur (MS) were compared to those of the recommended chemical fungicide Topsin-M 70 WP at a dose of 1000 µg/mL. They were evaluated in vitro and then in vivo at different temperatures (10 and 20 °C) on cucumber (Cucumis sativus) fruits. The total phenolic content (TPC) and total soluble solids (TSS) were determined to study the effects of various treatments on the shelf life of cucumber fruits, compared to untreated cucumber as a positive control. The diameters of S-NPs and Cu-NPs ranged from 10 to 50 nm, and 2 to 12 nm, respectively. The results revealed that S-NPs exhibited the highest antifungal activity, followed by Cu-NPs. However, CuSO₄ showed the lowest antifungal activity among all treatments. The antifungal activity of the prepared NPs increased with the increase in NP concentration, while the fungal growth was less at low temperature. The cytotoxicity of the prepared NPs was evaluated against the WI-38 and Vero cell lines in order to assess their applicability and sustainability. S-NPs caused less cytotoxicity than Cu-NPs.

It has become increasingly popular to replace chemically synthesized compounds with natural counterparts mostly found in natural sources, such as natural pigments. The conventional extraction processes for these compounds are limited by the toxicity and flammability of the solvents. To obtain pure extracts, it is always a longer process that requires several steps. Supercritical fluid extraction (SFE) is a cutting-edge green technology that is continuously increasing and expanding its fields of application, with benefits such as no waste produced, shorter extraction time, automation, and lower solvent consumption. The SFE of natural pigments has high potential in food, textiles, cosmetics, and pharmaceuticals; there are a number of other applications that can benefit from the SFE technique of natural pigments. The pigments that are extracted via SFE have a high potential for application and sustainability because of their biological and antimicrobial properties as well as low environmental risk. This review provides an update on the SFE technique, specifically as it pertains to the optimization of health-promoting pigments. This review focuses on antimicrobial pigments and the high efficiency of SFE in extracting pure antimicrobial pigments. In addition, the optimal conditions, biological activities, and possible applications of each category are explained.

The COVID-19 pandemic has clearly shown the importance of developing advanced protective equipment, and new antiviral fabrics for the protection and prevention of life-threatening viral diseases are needed. In this study, selenium nanoparticles (SeNPs) were combined with polyester fabrics using printing technique to obtain multifunctional properties, including combined antiviral and antibacterial activities as well as coloring. The properties of the printed polyester fabrics with SeNPs were estimated, including tensile strength and color fastness. Characterization of the SeNPs was carried out using TEM and SEM. The results of the analysis showed good uniformity and stability of the particles with sizes range from 40–60 nm and 40–80 nm for SeNPs 25 mM and 50 mM, respectively, as well as uniform coating of the SeNPs on the fabric. In addition, the SeNPs—printed polyester fabric exhibited high disinfection activity against severe acute respiratory syndrome coronavirus 2 (SARS-CoV-2) with an inhibition percentage of 87.5%. Moreover, a toxicity test of the resulting printed fabric revealed low cytotoxicity against the HFB4 cell line. In contrast, the treated fabric under study showed excellent killing potentiality against Gram-positive bacteria (Bacillus cereus) and Gram-negative bacteria (Pseudomonas aeruginosa, Salmonella typhi, and Escherichia coli). This multifunctional fabric has high potential for use in protective clothing applications by providing passive and active protection pathways.

Jojoba oil (JO) extracted from seeds has outstanding properties, including anti-inflammatory, antioxidant, and antibacterial activities, and can be stored forlong periodsof time. The unique properties of jojoba oil depend on its chemical composition; therefore, the effect of the jojoba genotype on the chemical properties and active components of the seed oil was evaluated in this study. Oil samples were collected from 15 elite Egyptian jojoba lines. The chemical composition, such as moisture, crude fiber, crude oil, ash, and crude protein of elite lines’ seeds was determined to investigate the variation among them based on the jojoba genotype. In addition, the iodine value was obtained to measure the degree of jojoba oil unsaturation, whereas the peroxide number was determined as an indicator of the damage level in jojoba oil. Fatty acid composition was studied to compare elite jojoba lines. Fatty acid profiles varied significantly depending on the jojoba genotype. Gadoleic acid exhibited the highest percentage value (67.85–75.50%) in the extracted jojoba oil, followed by erucic acid (12.60–14.81%) and oleic acid (7.86–10.99%). The iodine value, peroxide number, and fatty acid composition of the tested elite jojoba lines were compared withthose reported by the International Jojoba Export Council (IJEC). The results showed that the chemical properties of jojoba oils varied significantly, depending on the jojoba genotype.

The development of antibacterial coatings for footwear components is of great interest both from an industry and consumer point of view. In this work, the leather material was developed taking advantage of the intrinsic antibacterial activity and coloring ability of selenium nanoparticles (SeNPs). The SeNPs were synthesized and implemented into the leather surface by using ultrasonic techniques to obtain simultaneous coloring and functionalization. The formation of SeNPs in the solutions was evaluated using UV/Vis spectroscopy and the morphology of the NPs was determined by transmission electron microscopy (TEM). The treated leather material (leather/SeNPs) was characterized by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX). The effects of SeNPs on the coloration and antibacterial properties of the leather material were evaluated. The results revealed that the NPs were mostly spherical in shape, regularly distributed, and closely anchored to the leather surface. The particle size distribution of SeNPs at concentrations of 25 mM and 50 mM was in the range of 36–77 nm and 41–149 nm, respectively. It was observed that leather/SeNPs exhibited a higher depth of shade compared to untreated ones, as well as excellent fastness properties. The results showed that leather/SeNPs can significantly enhance the antibacterial activity against model of bacteria, including Gram-positive bacteria (Bacillus cereus) and Gram-negative bacteria (Pseudomonas aeruginosa, Salmonella typhi and Escherichia coli). Moreover, the resulting leather exhibited low cytotoxicity against HFB4 cell lines. This achievement should be quite appealing to the footwear industry as a way to prevent the spread of bacterial infection promoted by humidity, poor breathability and temperature which promote the expansion of the microflora of the skin.

Pine wood (PW) and beech wood (BW) are the most used wood in furniture and other applications owing to their unique characteristics and low machining cost. However, their biodegradability and varied moisture content limit their wider use and durability. Therefore, in this study, nanotechnology was used as a novel eco-friendly approach to enhance the durability, antimicrobial properties, and color of wood. Selenium nanoparticles (Se-NPs) were prepared in spherical shape at varied concentrations (25 and 50 mM) using an eco-friendly method in the range of 35–80 and 40–155 nm, respectively. Se-NPs formation at the nanoscale was confirmed using UV/Vis analysis, transmission electron microscopy (TEM), and X-ray diffraction (XRD). The prepared Se-NPs were then impregnated into PW and BW for different periods ranging from 2 h to 1 week. The treated wood were then leached in distilled water for 14 days to eliminate excess Se-NPs from the wood surface. The treated wood surfaces were examined using energy-dispersive X-ray spectroscopy (EDX) and scanning electron microscopy (SEM). In addition, the depth of Se-NPs penetration into the treated wood at both tangential and radial sides was determined. Se-NPs impacts on the color properties, density, moisture content and antimicrobial activities of the treated wood were evaluated. PW treated with Se-NPs showed better antimicrobial and color characteristics than treated BW. PW samples immersed in 50 mM Se-NPs for 2 h showed the highest K/S values, whereas the highest antimicrobial values were obtained for those immersed at the same concentration for 2 days, and 1 week.