“Green chemistry” is a simple and easily reproductible method that provides nanoparticles characterized by better stability and good dispersion in an aqueous solution. Nanoparticles can be synthesized by algae, bacteria, fungi, and plant extracts. Ganoderma lucidum is a commonly used medicinal mushroom with distinctive biological properties, such as antibacterial, antifungal, antioxidant, anti-inflammatory, anticancer, etc. In this study, aqueous mycelial extracts of Ganoderma lucidum were used to reduce AgNO₃ to form silver nanoparticles (AgNPs). The biosynthesized nanoparticles were characterized by UV-visible spectroscopy, scanning electron microscopy (SEM), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR) analysis. The maximum UV absorption was obtained at 420 nm, which represents the specific surface plasmon resonance band for biosynthesized silver nanoparticles. SEM images showed particles as predominantly spherical, while FTIR spectroscopic studies illustrated the presence of functional groups that can support the reducing of ion Ag⁺ to Ag(0). XRD peaks ratified the presence of AgNPs. The antimicrobial effectiveness of synthesized nanoparticles was tested against Gram-positive and Gram-negative bacterial and yeasts strains. The silver nanoparticles were effective against pathogens, inhibiting their proliferation, and thus reducing the risk to the environment and to public health.

The green synthesis of metal nanoparticles has received substantial attention due to their applications in various domains. The aim of the study was to obtain silver nanoparticles (AgNPs) by green synthesis with filamentous fungi, such as Cladosporium cladosporoides, Penicillium chrysogenum, and Purpureocillium lilacinum. Fungal species were grown on nutrient media and aqueous mycelium extracts were used to reduce Ag⁺ to Ag (0). The silver nanoparticles were analyzed by various techniques, such as UV-Visible spectroscopy (UV-Vis), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM), dynamic light scattering (DLS), and Zeta potential. The formation of silver nanoparticles was confirmed by UV-Vis spectroscopy and the color change of the mixture containing metal precursor and aqueous mycelium extract. FTIR displayed different functional groups as capping and reducing agents for the biosynthesis of AgNPs. SEM and TEM provided information on the particles’ morphology. DLS diagrams indicated mean particle diameters in the 124–168 nm region. All biosynthesized AgNPs had negative zeta values, which is a sign of good stability. Silver nanoparticles were evaluated for antimicrobial activity, and the most active were those synthesized with metabolites from Cladosporium, leading to 93.75% inhibition of Staphylococcus aureus, 67.20% of Escherichia coli, and 69.56% of Candida albicans. With the highest microbial inhibition percentage and a very good Poly Dispersion Index (Pd I), Cladosporium cladosporoides was selected as an environmentally friendly source of silver nanoparticles that could be used as a potential antimicrobial agent.

The main goal of this study was to present a facile and inexpensive approach for the preparation of hybrid coatings by the deposition under ambient air conditions of silver-based silica materials on glass substrates, which can be used to improve solar cells’ performance. The silica materials containing silver nanoparticles (AgNPs) were synthesized by the hydrolytic condensation of tetraethylorthosilicate (TEOS), triethoxymethylsilane (MTES), and trimethoxyhexadecylsilane (HDTMES), under acidic conditions, at room temperature (25 ± 2 °C). The silver nitrate solution (AgNO₃, 0.1 wt. %) was used as a source of Ag⁺ ions. The final samples were investigated through Fourier Transform Infrared Spectroscopy–Attenuated Total Reflectance (FTIR–ATR), Transmission Electron Microscopy equipped with energy dispersive X–ray (TEM–EDX), UV–Vis spectroscopy, Atomic Force Microscopy (AFM), and Raman Spectroscopy (RS). The TEM images confirmed the formation of AgNPs and were found to be around 3 nm. It was observed that AgNPs were embedded in the silica matrix. EDX also confirmed the presence of the resulting AgNPs within the silica material. AFM images demonstrated that the morphology of the hybrid films’ surfaces can be changed as a function of sol–gel composition. RS analysis indicated that silanol groups were significantly present on the silver-based silica film surface. The UV–Vis spectra revealed that the hybrid coatings presented a reflectance of ~8%, at 550 nm. This study will enhance the value of nanocoating technology in optoelectronics, particularly in the development of nanostructures that improve the performance in thin-film solar cells.