A stronger, cooler wood: One good way to reduce the amount of cooling a building needs is to make sure it reflects away infrared radiation. Passive radiative cooling materials are engineered to do this extremely well. Li et al. engineered a wood through delignification and re-pressing to create a mechanically strong material that also cools passively. They modeled the cooling savings of their wood for 16 different U.S. cities, which suggested savings between 20 and 50%. Cooling wood would be of particular value in hot and dry climates. Science , this issue p. 760

Patternable transparent wood with a high transmittance is fabricated via a solar-assisted chemical brushing approach.

Current membrane distillation (MD) is challenged by the inefficiency of water thermal separation from dissolved solutes, controlled by membrane porosity and thermal conductivity. Existing petroleum-derived polymeric membranes face major development barriers. Here, we demonstrate a first robust MD membrane directly fabricated from sustainable wood material. The hydrophobic nanowood membrane had high porosity (89 ± 3%) and hierarchical pore structure with a wide pore size distribution of crystalline cellulose nanofibrils and xylem vessels and lumina (channels) that facilitate water vapor transportation. The thermal conductivity was extremely low in the transverse direction, which reduces conductive heat transport. However, high thermal conductivity along the fiber enables efficient thermal dissipation along the axial direction. As a result, the membrane demonstrated excellent intrinsic vapor permeability (1.44 ± 0.09 kg m⁻¹ K⁻¹ s⁻¹ Pa⁻¹) and thermal efficiency (~70% at 60°C). The properties of thermal efficiency, water flux, scalability, and sustainability make nanowood highly desirable for MD applications.

Wood-based hydrogel with a unique anisotropic structure is an attractive soft material, but the presence of rigid crystalline cellulose in natural wood makes the hydrogel less flexible. In this study, an all-wood hydrogel was constructed by cross-linking cellulose fibers, polyvinyl alcohol (PVA) chains, and lignin molecules through the Hofmeister effect. The all-wood hydrogel shows a high tensile strength of 36.5 MPa and a strain up to ~ 438% in the longitudinal direction, which is much higher than its tensile strength (~ 2.6 MPa) and strain (~ 198%) in the radial direction, respectively. The high mechanical strength of all-wood hydrogels is mainly attributed to the strong hydrogen bonding, physical entanglement, and van der Waals forces between lignin molecules, cellulose nanofibers, and PVA chains. Thanks to its excellent flexibility, good conductivity, and sensitivity, the all-wood hydrogel can accurately distinguish diverse macroscale or subtle human movements, including finger flexion, pulse, and swallowing behavior. In particular, when “An Qi” was called four times within 15 s, two variations of the pronunciation could be identified. With recyclable, biodegradable, and adjustable mechanical properties, the all-wood hydrogel is a multifunctional soft material with promising applications, such as human motion monitoring, tissue engineering, and robotics materials.