The use of green solvents satisfies safer chemical engineering practices and environmental security. Herein, myristic acid (MA)—a green diluent—was selected to prepare poly- (4-methyl-1-pentene) (PMP) membranes with bicontinuous porous structure via a thermally induced phase separation (TIPS) process to maintain a high gas permeability. Firstly, based on the Hansen solubility parameter ‘distance’, Ra, the effect of four natural fatty acids on the PMP membrane structure was compared and studied to determine the optimal green diluent, MA. The thermodynamic phase diagram of the PMP-MA system was calculated and presented to show that a liquid-liquid phase separation region could be found during the TIPS process and the monotectic point was around 34.89 wt%. Then, the effect of the PMP concentration on the morphologies and crystallization behavior was systematically investigated to determine a proper PMP concentration for the membrane preparation. Finally, PMP hollow fiber (HF) membranes were fabricated with a PMP concentration of 30 wt% for the membrane performance characterization. The resultant PMP HF membranes possessed good performances that the porosity was 70%, the tensile strength was 96 cN, and the nitrogen flux was 8.20 ± 0.10 mL·(bar·cm²·min)⁻¹. We believe that this work can be a beneficial reference for people interested in the preparation of PMP membranes for medical applications.

Nowadays, the standards of discharging are gradually becoming stricter, since much attention has been paid to the protection of natural water resources around the world. Therefore, it is urgent to upgrade the existing wastewater treatment plant (WWTP), to improve the effluent quality, and reduce the discharged pollutants to the natural environment. In this paper, taking the “Liaocheng UESH (UE Envirotech) WWTP in Shandong province of China” as an example, the existing problems and the detailed measures for a renovation were systemically discussed by technical and economic evaluation, before and after the renovation. During the renovation, the ultrafiltration membrane was added as the final stage of the designed process route, while upgrading the operation conditions of biochemical process at the same time. After the renovation, the removal rates of chemical oxygen demand (COD_cr), biochemical oxygen demand (BOD₅), total phosphorus (TP) and other major pollutants were improved greatly, and the results fully achieved the standards of surface water class IV. The ultrafiltration system performs a stable permeability around 1.5 LMH/kPa. Besides, the economic performance of the renovation was evaluated via the net present value (NPV) method. The result reveals that the NPV of the renovation of the WWTP within the 20 year life cycle is CNY 72.51 million and the overall investment cost can be recovered within the fourth year after the reoperation of the plant. This research does not only indicate that it is feasible to take an ultrafiltration membrane as the main technology, both from technical and economic perspectives, while upgrading the biochemical process section in the meantime, but also provides a new strategy for the renovation of existing WWTPs to achieve more stringent emission standards.

To achieve a cleaner production, pesticide wastewater with concentrated NaCl can be treated by using a bipolar membrane electrodialysis (BMED) and converted to NaOH and HCl, which minimizes acid and alkali consumption in a pesticide production process. However, ion-exchange membranes (IEMs) are vulnerable to fouling by phenolic substances present in the concentrated NaCl solutions. This work aimed to understand the performance and fouling mechanism of BMED from phenol during the desalination of NaCl and explore an effective cleaning method. The results firstly showed that for the NaCl solutions with higher phenol concentrations, the selectivity of the IEMs was reduced after processing six successive batches of BMED, which led to reverse migration of ions, organics leakage, and an obvious increase in the energy consumption and the concentration of generated acid and alkali. Secondly, IEMs characterization analysis detected that the structure of the IEMs was deformed, while phenol fouling deposits were observed on the surface and interior of the IEMs, especially for the anion exchange membranes (AEMs). Then, the results of soaking tests proved that the phenol could bring about swelling-like degradation to the AEMs and 0.1 wt.% NaOH solution was studied to be the optimized cleaning agent since the performance of the fouled IEMs in the short-running process could be recovered after 5 h of in situ cleaning that removed the phenol fouling deposits efficiently. Finally, the results of a long-running BMED operation treating NaCl solution containing 10 g/L phenol concentration showed that the IEMs were severely fouled, and the fouling was firstly due to the swelling-like mechanism during the initial 12 successive batches, and then should belong to the blockage-like mechanism during the following 20 successive batches. The seriously fouled IEMs could no longer be recovered even after a deep in situ cleaning. This research proves that under appropriate pretreatment or operating conditions, the BMED process is an alternative way of treating wastewater with high salinity and the presence of phenol molecules.

Polymer-based membranes have advanced or novel functions in the various membrane separation processes for liquid and gaseous mixtures, such as gas separation, pervaporation (PV), reverse osmosis (RO), nanofiltration (NF), ultrafiltration (UF), microfiltration (MF), and in other critical applications of membranes such as water purification, solvent concentration, and recovery