This study evaluates the performance of commercial reverse osmosis (RO) and nanofiltration (NF) membranes for the removal of metal ions from synthetic water and surface water carried from the north-west of Lake Tanganyika in the city of Uvira, in the east of the Democratic Republic of Congo. Metal ion analyses were performed by the standardized ICP-MS and ICP-OES methods. The RO membrane showed higher metal ion rejection in high-concentration solutions (synthetic samples) prepared in the laboratory as well as in low-concentration samples from real raw water collected near Lake Tanganyika. Rejection levels were higher than 98% for Cr³⁺, Pb²⁺, Cd²⁺, As³⁺, Ni²⁺, and Sb⁺³ ions in the synthetic solutions, and 99.2, 98.8, 98.6, 99.2, 98.4, and 98.8%, respectively, in the real samples. The concentrations of metals in the permeate varied depending on the feed concentration and were 0.15 to 1.02 mg/L, 0.33 to 22 mg/L, and 0.11 to 22 mg/L in RO, NF90, and NF270 membranes, respectively. Regarding the NF membranes, the rejection of Cr, Ni, and Cd ions was interesting: 98.2, 97.8, and 92.3%, respectively. However, it was lower for Pb, As, and Sb ions: 76.9, 52.5 and 64.1%, respectively. The flux of NF was 329 to 375 L/m².h, much higher than for RO membranes, which had a flux of 98 to 132 L/m².h. The studied membranes are thus a feasible solution to remove the studied metals from real water sources at low concentrations since they meet the standards of the World Health Organization on specific values assigned to chemicals from industrial sources and human habitation areas where these ions are present in drinking water.

A new crystallization process for sodium bicarbonate (NaHCO₃) was studied, proposing the use of osmotic membrane distillation crystallization. Crystallization takes place due to the saturation of the feed solution after water evaporation on the feed side, permeating through the membrane pores to the osmotic side. The process operational parameters, i.e., feed and osmotic velocities, feed concentration, and temperature were studied to determine the optimal operating conditions. Regarding the feed and osmotic velocities, values of 0.038 and 0.0101 m/s, respectively, showed the highest transmembrane flux, i.e., 4.4 × 10⁻⁸ m³/m²·s. Moreover, study of the temperature variation illustrated that higher temperatures have a positive effect on the size and purity of the obtained crystals. The purity of the crystals obtained varied from 96.4 to 100% In addition, the flux changed from 2 × 10⁻⁸ to 7 × 10⁻⁸ m³/m²·s with an increase in temperature from 15 to 40 °C. However, due to heat exchange between the feed and the osmotic solutions, the energy loss in osmotic membrane distillation crystallization is higher at higher temperatures.