A new crystallization process for sodium bicarbonate (NaHCO₃) was studied, proposing the use of osmotic membrane distillation crystallization. Crystallization takes place due to the saturation of the feed solution after water evaporation on the feed side, permeating through the membrane pores to the osmotic side. The process operational parameters, i.e., feed and osmotic velocities, feed concentration, and temperature were studied to determine the optimal operating conditions. Regarding the feed and osmotic velocities, values of 0.038 and 0.0101 m/s, respectively, showed the highest transmembrane flux, i.e., 4.4 × 10⁻⁸ m³/m²·s. Moreover, study of the temperature variation illustrated that higher temperatures have a positive effect on the size and purity of the obtained crystals. The purity of the crystals obtained varied from 96.4 to 100% In addition, the flux changed from 2 × 10⁻⁸ to 7 × 10⁻⁸ m³/m²·s with an increase in temperature from 15 to 40 °C. However, due to heat exchange between the feed and the osmotic solutions, the energy loss in osmotic membrane distillation crystallization is higher at higher temperatures.

Improving the absorption of visible light in photocatalysts could enhance photocatalytic reactions and reduce energy consumption, particularly in sunny regions like Ecuador. This study reports the synthesis of ZnO and ZnO nanoparticles doped with 1.5 at.% Er, 5 at.% Al, and 1.5 at.% Er, 5 at.% Al using the sol–gel method. The effect of doping on the structure, morphology, absorption spectra, and photocatalytic properties was analyzed by XRD, SEM, EDS, and UV-Vis spectrophotometry. XRD confirmed the presence of the wurtzite ZnO structure, and UV-Vis diffuse reflection spectra showed a red shift in the band gap for doped ZnO compared to pristine ZnO. Photocatalytic activity was evaluated through the degradation of methyl orange (MO) under artificial visible light and natural sunlight in Quito, Ecuador. ZnO doped with Er/Al nanoparticles exhibited significantly enhanced photocatalytic performance under solar light, suggesting the potential for replacing artificial light and reducing operating costs in photocatalytic processes. Moreover, all doped samples retained the antibacterial properties of ZnO against B. subtilis, and Er/Al co-doping improved the inhibition of E. coli compared to undoped ZnO.

Chitosan biopolymer membranes reinforced with channel-selective ZIF-8 nanofillers were developed and thoroughly characterized as separators for bioelectrochemical systems. This study explores the synergistic effect of incorporating ZIF-8 into a chitosan matrix to enhance membrane performance. Key properties including water retention, chemical and thermal stability, surface resistance, antifouling capacity, and ionic conductivity were evaluated and benchmarked against commercial Nafion-117 and nanofiltration (NF) membranes. The ZIF-8/chitosan composite membranes (ZIF-8/CS) demonstrated excellent water retention and structural stability under harsh conditions, along with significantly reduced surface resistance and effective rejection of organic contaminants and salts (NaCl, Na₂SO₄). Notably, the composite ZIF-8/CS membranes achieved an ionic conductivity of 0.099 S/cm, approaching the value of Nafion-117 (0.13 S/cm) and substantially surpassing that of the NF membrane (0.013 S/cm). These results indicate that ZIF-8-reinforced chitosan membranes present a promising, sustainable, and cost-effective alternative to traditional separators in bioelectrochemical applications.

Chitosan biopolymer membranes reinforced with channel-selective ZIF-8 nanofillers were developed and characterized for use as separators in bioelectrochemical systems. The study focused on the application of biopolymer chitosan in combination with ZIF-8 as nano reinforcement agents to improve membrane performance. Key properties such as water retention, chemical and thermal stability, surface resistance, antifouling ability, and ionic conductivity of the mixed matrix membranes (Composite ZIF-8/chitosan) were evaluated and compared with commercial Nafion-117 and nanofiltration (NF) membranes. The composite ZIF-8/chitosan membranes exhibited excellent water retention and structural stability under harsh conditions, while reducing surface resistance and effectively rejecting organic contaminants and salts (NaCl, Na₂SO₄). Impressively, the ionic conductivity reached 0.105 S/cm, which is similar to that of Nafion-117. These results suggest that biopolymer chitosan reinforced with ZIF-8 nanofillers offers a sustainable and cost-effective alternative for use as separators in bioelectrochemical systems applications.

Bioelectrochemical systems (BESs) are technologies capable of converting chemical energy into electrical energy or producing value-added compounds. These systems typically employ Nafion membranes as proton exchange separators; however, Nafion is costly and prone to fouling. In this study, mixed-matrix membranes (MMMs) based on chitosan and its derivatives, incorporated with Er- and Al-doped ZnO nanoparticles, were synthesized and evaluated. Key properties assessed included antimicrobial activity, antifouling behavior, chemical stability, water retention, and proton conductivity. The results demonstrated that the chitosan-based membranes doped with Er/Al/ZnO outperformed Nafion in terms of antifouling properties, water retention, and a protective effect on the surface of the membrane against Escherichia coli and Staphylococcus aureus, while exhibiting comparable proton conductivity and chemical stability.