The zone refining technology is considered to be one of the most effective means of purifying lanthanum. However, it is tough to obtain the temperature distribution of the molten region through experimental methods. In this study, finite element analysis was used to establish the zone refining simulation model, and the impurity distribution of lanthanum after purification was investigated experimentally. Good agreement between the simulated and experimental results was obtained. The effects of the current and the frequency on the temperature distribution and the width of the region were studied using the simulation model. Through the zone refining experiment, the impurity distributions under different widths of molten region were revealed. Finally, the influence of molten region width on the limiting distribution was calculated by solving the limiting distribution equation.

Lanthanum fluoride (LaF₃) thin films were deposited on the Ge substrate using the molybdenum boat evaporation method. The effect of films’ oxygen impurity on the infrared optical properties has been investigated for the first time in this report. With the increase in oxygen content in the films, the F content decreases, and the O/F ratio decreases from 0.160 to 0.055. XRD patterns reveal that the presence of O impurity destroys the crystal structure integrity of the LaF₃ films and leads to the intensification of infrared absorption. The average transmittance decreases from 58.1% to 52.2%, and the peak transmittance decreases from 59.9% to 54.5%. Additionally, the refractive index and extinction coefficient of LaF₃ films with different oxygen content are obtained by fitting the transmittance test data. The results show that the refractive index and extinction coefficient of the films in 8–12 μm increase with the increase in oxygen content, the average refractive index increases from 1.339 to 1.478, and the extinction coefficient increases from 0.001 to 0.030. In this paper, the influence of oxygen impurity in the LaF₃ film on its infrared optical properties is revealed, which lays a theoretical foundation for the development of high-performance LaF₃ infrared antireflective film.

In this paper, the purification of lanthanum was studied by using zone-refining technology. The equilibrium distribution coefficient of impurities was calculated using a liquidus slope method to reveal impurities’ distribution properties. Meanwhile, the analysis of impurities’ concentration distribution for Fe and Si has been investigated based on the SPIM model. The calculated findings based on SPIM were found to be in good agreement with the experimental results. In addition, the influence of the zone-refining rate and the number of passes on the purification of lanthanum were studied. It was found that after ten times of zone refining with a zone-refining rate of 5 mm/min, the contents of Fe and Si impurities in metal decreased to 4 and 2 ppm, respectively.