In this paper, biodegradable epoxidized natural rubber containing cyclic carbonate groups (CNR) was prepared by the reaction between epoxidized natural rubber (ENR) and carbon dioxide. Dynamic disulfide bonds and a boronic ester structure were successfully constructed and then the cross-linking network was formed by the thermally initiated “click” reaction between thiol groups of the cross-linker and the residual epoxy groups of ENR. As a result of the exquisite double dynamic covalent structure, the material exhibits high self-healing efficiency. Moreover, by virtue of the cyclic carbonate structure of the CNR, the natural rubber was confirmed to be biodegradable according to the biodegradable measurement. To the best of our knowledge, natural rubber with biodegradable and self-healing characteristics was obtained for the first time.

Microgels have unique and versatile properties allowing their use in forward osmosis areas as a draw agent. In this contribution, poly(4-vinylpyridine) (P4VP) was synthesized via RAFT polymerization and then grafted to a poly(N-Isopropylacrylamide) (PNIPAAm) crosslinking network by reverse suspension polymerization. P4VP was successfully obtained by the quasiliving polymerization with the result of nuclear magnetic resonance and gel permeation chromatography characterization. The particle size and particle size distribution of the PNIPAAm-g-P4VP microgels containing 0, 5, 10, 15 and 20 wt% P4VP were measured by means of a laser particle size analyzer. It was found that all the microgels were of micrometer scale and the particle size was increased with the P4VP load. Inter/intra-molecular-specific interactions, i.e., hydrogen bond interactions were then investigated by Fourier infrared spectroscopy. In addition, the water flux measurements showed that all the PNIPAAm-g-P4VP microgels can draw water more effectively than a blank PNIPAAm microgel. For the copolymer microgel incorporating 20 wt% P4VP, the water flux was measured to be 7.48 L∙m⁻²∙h⁻¹.