Aluminum nitride (AlN) ceramics were prepared by both Hot-pressing (HP) and Spark-Plasma-Sintering (SPS) using cerium oxide as the sintering aid. The characterization of AlN raw powder denoted the presence of an amorphous layer that led to the formation of aluminum oxide. During the sintering process, CeO₂ introduced as a sintering aid was reduced into Ce₂O₃. The latter reacted with aluminum oxide to form a transient liquid phase that promotes sintering by both HP and SPS. A reactional path leading to the formation of secondary phases, such as CeAlO₃ and CeAl₁₁O₁₈, has been proposed according to the pseudo-binary Al₂O₃ – Ce₂O₃. Ceramics obtained from HP and SPS are presented as similar, except for the secondary-phase distribution. The influences of secondary phase composition and distribution on electrical conductivity were evaluated by leakage current measurements. The mechanism of DC conduction and the global conductivity of ceramics were discussed according to the sintering process and the number of secondary phases.

Spark Plasma Sintering (SPS) has become a conventional and promising sintering method for powder consolidation. This study aims to well understand the mechanisms of densification encountered during SPS treatments, especially in the early stages of sintering. The direct current (DC) electrical behavior of copper granular medium is characterized. Their properties are correlated with their microstructural evolutions through post-mortem scanning electron microscope (SEM) observations to allow a thorough understanding of the involved Branly effect that is suspected to occur in SPS. The electrical response is studied by modifying the initial thickness of the oxide layer on particles surfaces and applying various mechanical loads on the granular medium. Without load and at low current, the measured quasi-reversible behavior is connected to the formation of spots at the microcontacts between the particles. By increasing the current, the Branly transition from an insulating to a conductive state suddenly occurs. The insulating oxide layer is destroyed, and micro-bridges are created. The application of a mechanical pressure strongly modifies the DC Branly effect. Increasing low stress leads to a strong decrease in the breakdown field. For high-applied pressure, successive drops in the electric field are detected during the electrical transition. These successive drops are induced by microcracking of the insulating oxide layer.

A complete methodology combining experiments and modeling has been developed to investigate the constrained sintering of low-temperature cofired ceramic (LTCC) systems. The thermomechanical and sintering behavior laws, previously identified for the selected commercial LTCC material, were implemented in a finite element model. The reliability and validity range of the built model has been investigated thanks to the development of a specific distortion experience. The distortion generated during the constrained sintering of a porous LTCC layer deposited on a dense one has been monitored in situ by ombroscopy. The measured camber evolution was compared with numerical results. The camber phenomena predicted numerically and observed experimentally are very similar, characterized by the onset of distortion around 918 K and a similar evolution during heating. However, at high temperatures (around 1100 K), the simulated camber slightly differs from the experimental one. It seems to be related to the damage to the dense LTCC layer by microcracking.