In this work, graphite intercalation compounds (GICs) were synthesized using three different oxidizers: (NH₄)₂S₂O₈, K₂S₂O₈, and CrO₃ with and without P₂O₅ as a water-binding agent. Furthermore, the samples obtained were heat-treated at 800 °C. Specimens were characterized by optical microscopy, Raman spectroscopy, Fourier transform infrared spectroscopy (FTIR), X-ray powder diffraction (XRD), and scanning electron microscopy (SEM). The correlation between different characteristic parameters of the Raman analysis has shown that the use of CrO₃ results in a much higher structural disorder compared to the products obtained using persulfate oxidizers. Narrowing the correlation set revealed that minimal defect concentration can be reached by using K₂S₂O₈, while the use of (NH₄)₂S₂O₈ causes a slightly higher concentration of defects. It was also established that the additional use of P₂O₅ can help to achieve more effective intercalation and has a positive effect on the formation of the stage I GIC phase. After heat treatment, the intercalated products mostly return to a graphite-like structure; however, the samples obtained with CrO₃ stand out with the most significant changes in their surface morphology. Therefore, analysis suggests that GICs obtained using persulfate oxidizers and P₂O₅ could be a candidate to produce high-quality graphene or graphene oxide.

Graphene-polypyrrole (GP) nanocomposites were synthesized by a wet-way protocol using a graphite bisulfate (GBS) precursor. Consequently, GBS, a type of graphite intercalation compound, was prepared in the presence of concentrated sulfuric acid in the presence of a potassium periodate oxidizer. Three different types of graphite precursor with particle sizes of <50 μm, ≥150, ≤830 μm, and ≤2000 μm were used for this purpose. It was found that in the Raman spectra of GBS samples, the characteristic D band, which is caused by defects in the graphene layer, disappears. Therefore, the proposed synthesis protocol of GBS could be considered as a prospective intermediate stage in the preparation of graphene with low defect concentration. In contrast to alkali metal intercalation, the intercalation process involving anions with a relatively complex structure (e.g., HSO₄⁻), which has been much less studied and requires further research. On the basis of the results obtained, structural models of graphite intercalation compounds as well as GP nanocomposites were discussed. The most relevant areas of application for GP nanocomposites, including energy storage and (bio)sensing, were considered. This work contributes to the development of cost-effective, scalable, and highly efficient intercalation methods, which still remain a significant challenge.