Polyglycolic acid (PGA) is used as a reinforcing component to enhance the mechanical properties of poly(ethylene glycol-co-cyclohexane-1,4-dimethanol terephthalate) (PETG). The tensile performance, micromorphology, crystallinity, heat resistance, and melt mass flow rates (MFRs) of PETG/PGA blends with varying PGA contents were studied. Both the tensile yield strength and tensile modulus of the PETG/PGA blends increased gradually with an increase in the PGA content from 0 to 35 wt%. The tensile yield strength of the PETG/PGA (65/35) blend increased by 8.7% (44.38 to 48.24 MPa), and the tensile modulus increased by 40.2% (1076 to 1509 MPa). However, its tensile ductility decreased drastically, owing to the poor interfacial compatibility of PETG/PGA and the oversized PGA domains. A multiple epoxy chain extender (ADR) was introduced into the PETG/PGA (65/35) blend to improve its interfacial compatibility and rheological properties. The tensile performance, micromorphology, rheological properties, crystallinity, and heat resistance of PETG/PGA (65/35) blends with varying ADR contents were studied. The strong chain extension effect of ADR along with its reactive compatibilization improved the rheological properties and tensile ductility. By carefully controlling the ADR concentration, the performance of PETG/PGA blends can be regulated for different applications.

The combined influences of crystallinity and reactive compatibilizer—a multifunctional epoxide (ADR)—on morphology, tensile performance, and heat resistance of polylactide/thermoplastic polyester elastomer (PLA/TPEE) (80/20) blends were investigated. Annealing involved an isothermal cold crystallization of PLA matrix was performed to increase crystallinity of the samples. First, isothermal cold crystallization kinetics were investigated using differential scanning calorimetry measurement. It was found that the addition of ADR decreased the crystallization rate of the samples. The maximum crystallinity of the annealed samples also decreased from 40% to 34% while ADR loading increased from zero to 1.0 phr. Furthermore, influence of crystallinity on mechanical performances of the PLA/TPEE sample was researched. The heat resistance of the sample showed a significant enhancement while increasing its crystallinity. Meanwhile, the tensile ductility of the crystallized PLA/TPEE sample became very poor due to the embrittlement with increased crystallinity and the incompatibility between PLA and TPEE. However, the annealed PLA/TPEE/ADR samples with high crystallinity kept a higher tensile ductility because ADR greatly improved the interfacial compatibility. Differences in tensile fracture behaviors of the quenched and annealed PLA/TPEE samples with and without ADR were discussed in detail. At last, crystallized PLA/TPEE/ADR blends with excellent heat resistance and high tensile ductility were obtained by annealing and reactive compatibilization.

This study investigated the impact of a multiple epoxy chain extender (ADR) on the rheological behavior, crystallization, and mechanical properties of polyglycolic acid (PGA). Tests of the torque and melt mass flow rate and dynamic rheological analysis were conducted to study the rheological behavior of PGA modified with ADR. The rheological results of the modified PGA showed a significantly increased viscosity and storage modulus with an increase in the ADR amount, which could be attributed to the chain extension/branching reactions between PGA and ADR. It was proved that ADR could be used as an efficient chain extender for tailoring the rheological performance of PGA. The Han plot of the modified PGA showed a transition of viscous behavior to elastic behavior, while the ADR content was increased from 0 to 0.9 phr. The formation of long-chain branches (LCBs) was confirmed via the Cole–Cole plot and weighted relaxation spectrum, wherein the LCBs substantially changed the rheological behavior of the modified PGA. The vGP plots predicted a star-type topological structure for the LCBs. The results of non-isothermal crystallization kinetics suggested that the crystallization of the modified PGA was predominantly homogeneous nucleation and three-dimensional growth. The crystallinity decreased slightly with the increase in the ADR amount. Compared to neat PGA, the modified PGA samples exhibited better tensile and flexural performances.