This study aims to investigate the applicability of a hybrid electrochemical sensor composed of cork and graphite (Gr) for detecting caffeine in aqueous solutions. Raw cork (RAC) and regranulated cork (RGC, obtained by thermal treatment of RAC with steam at 380 °C) were tested as modifiers. The results clearly showed that the cork-graphite sensors, GrRAC and GrRGC, exhibited a linear response over a wide range of caffeine concentration (5–1000 µM), with R² of 0.99 and 0.98, respectively. The limits of detection (LOD), estimated at 2.9 and 6.1 µM for GrRAC and GrRGC, suggest greater sensitivity and reproducibility than the unmodified conventional graphite sensor. The low-cost cork-graphite sensors were successfully applied in the determination of caffeine in soft drinks and pharmaceutical formulations, presenting well-defined current signals when analyzing real samples. When comparing electrochemical determinations and high performance liquid chromatography measurements, no significant differences were observed (mean accuracy 3.0%), highlighting the potential use of these sensors to determine caffeine in different samples.

Biopolymer films have several industrial applications because they are environmentally sustainable. Cassava starch is a biopolymer that is easily available, but has limitations: it is hydrophilic, poorly resistant and degradable. The improvement of these properties was proposed in this research from the use of bentonite clay (BT) as a filling material. The compatibilization of this in the polymer matrix was obtained by ion exchange with an organic anionic surfactant. The formation of intercalated or exfoliated starch nanocomposites in the presence of natural or modified clay was characterized by XRD, FTIR, AFM and SEM. The improvement of water vapor, thermal and mechanical properties was investigated by WVP, solubility, TGA and tensile test. The starch nanocomposites in the presence of modified clay showed a better result than those of natural clay. There was no significant difference in the color of the starch film in the presence of the natural or modified clay.