A one-step carbothermal synthesis and characterization of biochar-supported nanoscale zero-valent iron (nZVI/BC) was performed for the removal of hexavalent chromium (Cr(VI)) from aqueous solution. High dispersions of nanoscale zero-valent iron supported on biochar were successfully synthesized by the pyrolysis of an iron-impregnated biomass (corn stover) as the carbon and iron source under nitrogen atmosphere. The effects of the pyrolytic temperature on the Fe mineralogies formed on the biochar are discussed. In general, the effects of the treatment time, initial solution pH, and nZVI/BC dosage on the Cr(VI) removal are presented. The results showed high crystallinity and purity, and nZVI/BC was obtained at a pyrolytic temperature of 800 °C. The batch experimental results determined that the adsorption capacity of Cr(VI) decreases with the increase in the initial pH value from 4.0 to 10.0. The Cr(VI) adsorption kinetics data effectively followed a pseudo-second-order kinetics with a calculated rate constant of 0.0.3396 g mg⁻¹ min⁻¹. The calculated thermodynamic parameters, such as ΔG°, ΔH°, and ΔS°, were evaluated, and the results indicated that the Cr(VI) reduction on nZVI/BC was a spontaneous and endothermic process. The adsorption mechanism of Cr(VI) was investigated by XRD and XPS analyses and the results demonstrated that Cr(VI) was reduced to Cr(III) and the oxidation of nZVI occurred during the reaction process. These results prove that nZVI/BC synthesized by a one-step carbothermal method can be considered as a potential candidate for the removal of Cr(VI) from aqueous solutions.

Arsenic (As) contamination of surface water has become a global concern, especially for the third world countries, and it is imperative to develop advanced materials and an effective treatment method to address the issue. In this paper, iron doped ZIF-8@MXene (Fe-ZIF-8@MXene) was prepared as a potential adsorbent to effectively and simultaneously remove As(III/V) from wastewater. To investigate this, Fe-ZIF-8@MXene was characterized before and after the removal of mixed As(III/V). The results of Fourier transform infrared (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), specific surface area (BET) and point of zero charge (pHpzc) showed that Fe-ZIF-8@MXene was prepared successfully and kept a stable structure after As(III) and As(V) adsorption. The particle size of Fe-ZIF-8@MXene was in the range of 0.5 μm to 2.5 μm, where its BET was 531.7 m²/g. For both contaminants, adsorption was found to follow pseudo-second-order kinetics and was best-fitted by the Langmuir adsorption model with correlation coefficients (R²) of 0.998 and 0.997, for As(III) and As(V), respectively. The adsorbent was then applied to remove As from two actual water samples, giving maximum removal rates of 91.07% and 98.96% for As(III) and As(V), respectively. Finally, removal mechanisms for As(III/V) by Fe-ZIF-8@MXene were also explored. During the adsorption, multiple complexes were formed under the effect of its abundant surface functional groups involving multiple mechanisms, which included Van der Waals force, surface adsorption, chemical complexation and electrostatic interactions. In conclusion, this study demonstrated that Fe-ZIF-8@MXene was an advanced and reusable material for simultaneous removal of As(III/V) in wastewater.

Biochar prepared from crop straw is an economical method for adsorbing bromocresol green (BCG) from textile industrial wastewater. However, there is limited research on the adsorption mechanism of biochar for the removal of BCG. This study utilized cucumber straw as raw material to prepare biochar with good adsorption potential and characterized its physicochemical properties. Through adsorption experiments, the effects of solution pH, biochar dosage, and initial dye concentration on adsorption performance were examined. The adsorption mechanism of cucumber straw biochar (CBC) for BCG was elucidated at the molecular level using adsorption kinetics, adsorption isotherm models, and density functional theory (DFT) calculations. Results show that the specific surface area of the CBC is 101.58 m²/g, and it has a high degree of carbonization, similar to the structure of graphite crystals. The presence of aromatic rings, –OH groups, and –COOH groups in CBC provides abundant adsorption sites for BCG. The adsorption process of CBC for BCG is influenced by both physical and chemical adsorption, and can be described by the Langmuir isotherm model, indicating a monolayer adsorption process. The theoretical maximum monolayer adsorption capacity (q_m) of BCG at 298 K was calculated to be 99.18 mg/g. DFT calculations reveal interactions between BCG and CBC involving electrostatic interactions, van der Waals forces, halogen–π interactions, π–π interactions, and hydrogen bonds. Additionally, the interaction of hydrogen bonds between BCG and the –COOH group of biochar is stronger than that between BCG and the –OH group. These findings provide valuable insights into the preparation and application of efficient organic dye adsorbents.