We demonstrate a simple and low cost mode-locked erbium-doped fiber laser (EDFL) operating in the nanosecond region using a single-walled carbon nanotube (SWCNT)-based saturable absorber (SA). A droplet of SWCNT solution is applied on the end of a fiber ferrule, which is then mated to another clean connector ferrule to construct an SA. Then the SA is integrated into a ring EDFL cavity for nanosecond pulse generation. The EDFL operates at around 1570.4 nm, with a soliton-like spectrum with small Kelly sidebands, which confirms the attainment of the anomalous dispersion. It produces a soliton pulse train with a 332 ns width, repetition rate of 909.1 kHz, an average output power of 0.31 mW, and energy of 0.34 nJ at the maximum pump power of 130.8 mW.

The incoming 5G technology requires antennas with a greater capacity, wider wireless spectrum utilisation, high gain, and steer-ability. This is due to the cramped spectrum utilisation in the previous generation. As a matter of fact, conventional antennas are unable to serve the new frequency due to the limitations in fabrication and installation mainly for smaller sizes. The use of graphene material promises antennas with smaller sizes and thinner dimensions, yet capable of emitting higher frequencies. Hence, graphene antennas were studied at a frequency of 15 GHz in both single and array elements. The high-frequency antenna contributed to a large bandwidth and was excited by coplanar waveguide for easy fabrication on one surface via screen printing. The defected ground structure was applied in an array element to improve the radiation and increase the gain. The results showed that the printed, single element graphene antenna produced an impedance bandwidth, gain, and efficiency of 48.64%, 2.87 dBi, and 67.44%, respectively. Meanwhile, the array element produced slightly better efficiency (72.98%), approximately the same impedance bandwidth as the single element (48.98%), but higher gain (8.41 dBi). Moreover, it provided a beam width of 21.2° with scanning beam capability from 0° up to 39.05°. Thus, it was proved that graphene materials can be applied in 5G.

An optical fiber humidity sensor was fabricated using a hydrophilic gel (agarose) deposited on the tapered plastic optical fiber (POF). The sensing element, agarose, can absorb and exude moisture from/to the ambience, thereby altering its refractive index and changing its ability to modulate the intensity of light that propagates through the fiber. Thus, the operating principle of the sensor is based on the intensity modulation technique, which utilizes a tapered POF probe coated with agarose that is sensitive to humidity. The POF, which was fabricated using an etching method, has a waist diameter of 0.45 mm and tapering length of 10 mm. As the relative humidity varies from 50% to 80%, the output voltage of the sensor with agarose gel of 0.5% weight content decreases linearly from 2.24 mV to 1.55 mV. The agarose-based sensor produces a sensitivity of 0.0228 mV/%, with a slope linearity of more than 98.36%. The tapered fiber with agarose gel of 1% weight content produces a sensitivity of 0.0103 mV/% with a slope linearity of more than 94.95% and a limit of detection of 2.635%, while the tapered fiber with agarose gel of 1.5% weight content produces a sensitivity of 0.0079 mV/% with a slope linearity of more than 98.53% and a limit of detection of 6.853%. The fiber with agarose gel of 0.5% weight content shows higher sensitivity compared to that of 1% and 1.5% due to the effect of pore size, which changes with concentration. The results demonstrate that agarose-based optical fiber sensors are both sensitive and efficient for economical and flexible measurements of humidity.

This study investigated the different thicknesses of TiO₂ photoanode films and the effect of surface plasmon resonance (SPR) of Ag-TiO₂ nanocomposites on the current-voltage (I–V) performance of dye-sensitized solar cells (DSSC). The TiO₂ layer was deposited using the doctor blade technique and the thickness of the TiO₂ films was controlled by using a different number of Scotch tape layers. The silver nanoparticles (AgNP) were synthesised using a chemical reduction method and the concentration of sodium citrate as a reducing agent was varied from 4 to 12 mM to study the effect of citrate ion on the size of the nanoparticles. Ag-TiO₂ nanopowder was prepared by adding pure anatase TiO₂ powder into AgNP colloidal solution. The mixture was left to dry for 24 h to obtain Ag-TiO₂ powder for paste preparation. The three-layer Scotch tape, with thickness of 14.38 µm, achieved a high efficiency of 4.14%. This results showed that three layers was the optimal thickness to improve dye loading and to reduce the charge recombination rate. As for the Ag-TiO₂ nanocomposites, 10 mM of AgNP, with a mean diameter of 65.23 nm and high efficiency of 6.92%, proved that SPR can enhance the absorption capability of dye and improve the photon-to-electron generation.