One of the main challenges in experimental fracture mechanics is to correctly estimate fracture parameters of a nonhomogeneous and nonlinear material under large deformation. The crack tip detection is strongly affected by fibers at crack tip, leading to inaccurate measures. To overcome this limitation, a novel methodology based on the Digital Image Correlation (DIC) method for crack tip detection of fibrous soft composites is proposed in this work. The unidirectional composite was manufactured using a matrix of polydimethylsiloxane reinforced with a single layer of extensible cotton knit fabric. For two different fiber orientations, the crack growth ($da$), Crack Tip Opening Displacement (CTOD) and Crack Tip Opening Angle (CTOA) were determined using pure shear specimens under mode I fracture. A consistent estimation of fracture parameters was obtained. The location of the crack tip position during the fracture test using the DIC-based methodology was validated against a visual inspection approach. Results indicated that the DIC-based methodology is easily replicable, precise and robust.

Additive manufacturing (AM) is revolutionizing the fabrication of metallic components, offering significant potential to compete with or complement traditional casting, forging, and machining processes, and enabling the production of complex functional components. Recent advancements in AM technology have facilitated the processing of shape memory alloys (SMAs) with functional properties comparable to those of conventionally processed alloys. However, the AM of NiTi SMAs remains underexplored due to the extreme complexity of the process, high melting point, and reactivity with oxygen. This study investigates the impact of AM processing on the shape memory properties of NiTi alloys using the Micro Wire and Arc Directed Energy Deposition (μ-WA-DED) technique in short circuit mode with a pioneering 0.3 mm pre-alloyed wire, focusing on increasing precision and control in the deposition process. The macroscopic morphology, microstructure, phase composition, phase-transformation temperatures, and mechanical properties of each deposited layer were analyzed. Results indicated austenite (B2) as the predominant phase, with retained martensite (B19′) and a reversible martensitic transformation (B2 ⇌ B19′) in the second layer. Mechanical characterization revealed variations in hardness (H) and elastic modulus (E) due to microstructural heterogeneity and composition. The first layer exhibited H = 3.8 GPa and E = 70 GPa, associated with the B2-NiTi phase, while higher values were obtained in the second layer, i.e., E = 100 GPa and H = 7 GPa. This study establishes for the first time the feasibility of NiTi alloy deposition with a 0.3 mm wire, setting a new standard for future research and applications in AM using μ-WA-DED.