Glassy hydrocarbon-based membranes are being researched as a replacement for perfluorosulfonic acid (PFSA) membranes in proton exchange membrane water electrolysis (PEMWE). Here, naphthalene containing Poly(arylene Ether Ketone) was introduced into the Poly(p-phenylene)-based multi-block copolymers through Ni(0)-catalyzed coupling reaction to enhance π-π interactions of the naphthalene units. It is discovered that there is an optimum input ratio of the hydrophilic monomer and NBP oligomer for the multi-block copolymers with high ion exchange capacity (IEC) and polymerization yield. With the optimum input ratio, the naphthalene containing copolymer exhibits good hydrogen gas barrier property, chemical stability, and mechanical toughness, even with its high IEC value over 2.4 meq g⁻¹. The membrane shows 3.6 times higher proton selectivity to hydrogen gas than Nafion 212. The PEMWE single cells using the membrane performed better (5.5 A cm⁻²) than Nafion 212 (4.75 A cm⁻²) at 1.9 V and 80 °C. These findings suggest that naphthalene containing copolymer membranes are a promising replacement for PFSA membranes in PEMWE.

A new hydrocarbon-based (HC) composite membrane was developed using liquid crystal polymer (LCP)-nonwoven fabrics for application in proton exchange membrane water electrolysis (PEMWE). A copolymer of sulfonated poly(arylene ether sulfone) with a sulfonation degree of 50 mol% (SPAES50) was utilized as an ionomer for the HC membranes and impregnated into the LCP-nonwoven fabrics without any surface treatment of the LCP. The physical interlocking structure between the SPAES50 and LCP-nonwoven fabrics was investigated, validating the outstanding mechanical properties and dimensional stability of the composite membrane in comparison to the pristine membrane. In addition, the through-plane proton conductivity of the composite membrane at 80 °C was only 15% lower than that of the pristine membrane because of the defect-free impregnation state, minimizing the decrease in the proton conductivity caused by the non-proton conductive LCP. During the electrochemical evaluation, the superior cell performance of the composite membrane was evident, with a current density of 5.41 A/cm² at 1.9 V, compared to 4.65 A/cm² for the pristine membrane, which can be attributed to the smaller membrane resistance of the composite membrane. From the results of the degradation rates, the prepared composite membrane also showed enhanced cell efficiency and durability during the PEMWE operations.

Achieving high ionic conductivity, wide voltage window, and good mechanical strength in a single material remains a key challenge for polymer-based electrolytes for use in solid-state supercapacitors (SCs). Herein, we report cross-linked composite gel polymer electrolytes (CGPEs) based on multi-cross-linkable H-shaped poly(ethylene oxide)–poly(propylene oxide) (PEO-PPO) tetrablock copolymer precursors, SiO₂ nanoparticles, and 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide, an ionic liquid (IL). Self-standing CGPE membranes with a high IL content were prepared using in situ cross-linking reactions between the silane groups present in the precursor and the SiO₂ surface. The incorporation of an optimal amount of SiO₂ increased the cross-linking density of the resulting CGPE while reducing polymer-chain ordering and, consequently, increasing both ionic conductivity and mechanical strength. As a result, the CGPE with 0.1 wt % SiO₂ exhibited a high ionic conductivity (2.22 × 10^–3 S cm^–1 at 25 °C), good tensile strength (453 kPa), and high thermal stability up to 330 °C. Finally, an all-solid-state SC assembled with the prepared CGPE showed a high operating voltage (3 V), a large specific capacitance (103.9 F g^–1 at 1 A g^–1), and excellent durability (94% capacitance retention over 10,000 charge/discharge cycles), which highlights its strong potential as a solid-state electrolyte for SCs.