It is well known that silicon-rich oxide (SRO) shows intense photoluminescence (PL). In this work, the authors studied the relationship of the surface morphology and the PL emission. PL spectra of SRO as a function of the excess silicon, temperature, and time of thermal annealing were obtained. The same samples were studied using transmission electronic microscopy and atomic force microscopy to determine their microstructure and surface morphology. A relationship between silicon agglomerates in the SRO and the surface morphology was obtained. Then, the red PL emission was related to the surface morphology. The authors found that the surface roughness is an important parameter for the high red emission of SRO.

Motivated by the necessity to have all silicon optoelectronic circuits, researchers around the world are working with light emitting silicon materials. Such materials are silicon dielectric compounds with silicon content altered, such as silicon oxide or nitride, enriched in different ways with Silicon. Silicon Rich Oxide or silicon dioxide enriched with silicon, and silicon rich nitride are without a doubt the most promising materials to reach this goal. Even though they are subjected to countless studies, the light emission phenomenon has not been completely clarified. So, a review of different proposals presented to understand the light emission phenomenon including emissions related to nanocrystals and to point defects in SiO₂ is presented.

An in-depth study of the physical and electrical properties of Si-nanocrystal-based MOSLEDs is presented. The active layers were fabricated with different concentrations of Si by both ion implantation and plasma-enhanced chemical vapour deposition. Devices fabricated by ion implantation exhibit a combination of direct current and field-effect luminescence under a bipolar pulsed excitation. The onset of the emission decreases with the Si excess from 6 to 3 V. The direct current emission is attributed to impact ionization and is associated with the reasonably high current levels observed in current-voltage measurements. This behaviour is in good agreement with transmission electron microscopy images that revealed a continuous and uniform Si nanocrystal distribution. The emission power efficiency is relatively low, approximately 10(-3)%, and the emission intensity exhibits fast degradation rates, as revealed from accelerated ageing experiments. Devices fabricated by chemical deposition only exhibit field-effect luminescence, whose onset decreases with the Si excess from 20 to 6 V. The absence of the continuous emission is explained by the observation of a 5 nm region free of nanocrystals, which strongly reduces the direct current through the gate. The main benefit of having this nanocrystal-free region is that tunnelling current flow assisted by nanocrystals is blocked by the SiO2 stack so that power consumption is strongly reduced, which in return increases the device power efficiency up to 0.1%. In addition, the accelerated ageing studies reveal a 50% degradation rate reduction as compared to implanted structures.