Potentiostatic electrodeposition was used to obtain CoCrFeMnNi high-entropy alloy (HEA) thin films on copper substrate. An electrolyte based on a DMSO (dimethyl sulfoxide)-CH₃CN (acetonitrile) organic compound was used for the HEA deposition. The microstructure of the high-entropy deposits before and after corrosion in artificial seawater was investigated by scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS) investigation. SEM analysis revealed that compact and uniform film consists of compact and uniform 50 nm–5 μm particles that form the HEA films. The successful co-deposition of all five elements was highlighted by the energy dispersive spectrometry investigation (EDS). Electrochemical measurements carried out in an aerated artificial seawater solution under ambient conditions demonstrated the promising potential for application in the field of anti-corrosion protection, due to the protective behavior of the HEA thin films.

In this paper, we investigate what effects heat treatment can have on potentiodynamically electrodeposited high-entropy thin film (HEA) CoCrFeMnNi alloys. We focused our study on the corrosion resistance in synthetic seawater, corroborated with the structure and microstructure of these thin films. Thin films of HEA alloys were deposited on a copper foil substrate, using an electrolyte based on the organic system dimethyl-sulfoxide (DMSO-(CH₃)₂SO)-acetonitrile (AN-CH₃CN) (in a volume ratio of 4:1), which contains LiClO₄ as electrolyte support and chloride salts of CoCl₂, CrCl₃ × 6H₂O, FeCl₂ × 4H₂O, MnCl₂ × 4H₂O and NiCl₂ × 6H₂O. Using MatCalc PC software, based on the CALPHAD method, the structure and characteristics of the HEA system were investigated, and thermodynamic and kinetic criteria were calculated. The modeling process generated in the body-centered-cubic (BCC) or face-centered-cubic (FCC) structures a series of optimal compositions that are appropriate to be used in anticorrosive and tribological applications in a marine environment. Electrochemical measurements were carried out in an aerated artificial seawater solution at ambient temperature. In the experimental media, HEA thin films proved to have good corrosion resistance and were even better than the copper substrate. Corrosion resistance was improved after heat treatment, as shown by polarization and EIS tests. The structure and microstructure of HEA thin films before and after corrosion in artificial seawater were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS). The XRD data showed no significant changes in the structure of HEA heat-treated thin films after the corrosion in saline media. The data obtained by polarization and ESI are supported by results from SEM-EDS. This complex study reveals that, for HEA thin films, heat treatment leads to an increase in corrosion resistance. So, this finding suggests that thermal annealing is an appropriate method for improving the corrosion performance of HEA thin films.

Materials used in the marine industry are exposed to extreme conditions, so it is necessary to meet remarkable characteristics, such as mechanical resistance, low density, and good corrosion resistance. The challenging environment requires continuous performance improvements, so this work is focused on developing new materials with superior properties, using the electrochemical deposition technique, which are convenient for marine engineering. High-entropy alloys have been attracting tremendous interest in many applications, due to their simple crystal structures and advantageous physical-chemical properties, such as high strength, anti-corrosion, erosion, and electro-magnetic capabilities. To identify the most appropriate compositions, MatCalc software was used to predict the structure and characteristics of the required materials, and thermodynamic and kinetic criteria calculations were performed. The modelling processes generated a series of optimal compositions in the AlCrCuFeNi alloy system, that are suitable to be used in anticorrosive and tribological applications. The composition and morphology of the obtained high entropy alloy thin films revealed a uniform structure, with a small grain profile. The corrosion resistance was investigated in artificial seawater to observe the behavior of the newly developed materials in demanding conditions, and the results showed improved results compared to the copper foil substrate.

We investigate the corrosion behavior on the microstructure of CoCrFeMnNi high-entropy thin film potentiodynamic alloys electrodeposited on aluminum support. Using electrolytes based on dimethyformamide (DMF), (HCON(CH₃)₂), dimethylsulfoxide (DMSO, (CH₃)₂SO), an acetonitrile (AN, CH₃CN) organic system (4:1 vol. ratio), LiClO₄ in different concentrations and CoCl₂, CrCl₃ × 6H₂O, FeCl₂ × 4H₂O, MnCl₂ × 4H₂O and NiCl₂ × 6H₂O in different conditions, the HEA components were co-deposited on an aluminum foil substrate. Using the CALPHAD method and the MatCalc PC software, the structure of the HEA system under study was investigated by calculating the characteristic kinetic and thermodynamic criteria. The influence of each metal from HEA inside the solid solution zone and over the formation of the solid solution phase were obtained from the ratio between the derived parameters. The electrochemical measurements, which demonstrate that on an aluminum support the HEA thin films have lower corrosion resistance, were performed at ambient temperature in an aerated artificial solution. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) were used to investigate the microstructure of HEA thin films before and after corrosion in artificial seawater. This complex study demonstrates that the electrodeposition of HEA thin films on an aluminum support is more difficult and that the resistance to corrosion is much lower compared to that in the previous work on HEA deposits on a copper support.

Complex concentrated alloys (CCAs) are a new family of materials with near equimolar compositions that fluctuate depending on the characteristics and destination of the material. CCAs expand the compositional limits of the traditional alloys, displaying new pathways in material design. A novel light density Al₅Cu_0.5Si_0.2Zn_1.5Mg_0.2 alloy was studied to determine the structural particularities and related properties. The alloy was prepared in an induction furnace and then annealed under a protective atmosphere. The resulted specimens were analysed by chemical, structural, mechanical, and corrosion resistance. The structural analyses revealed a predominant FCC and BCC solid solution structure. The alloy produced a compression strength of 500–600 MPa, comparable with conventional aluminium alloys. The corrosion resistance in 3.5% NaCl solution was 0.3424 mm/year for as-cast and 0.1972 mm/year for heat-treated alloy, superior to steel, making the alloy a good candidate for marine applications.