The aim of this review is to bring together the main natural polymer applications for environmental remediation, as a class of nexus materials with advanced properties that offer the opportunity of integration in single or simultaneous decontamination processes. By identifying the main natural polymers derived from agro-industrial sources or monomers converted by biotechnology into sustainable polymers, the paper offers the main performances identified in the literature for: (i) the treatment of water contaminated with heavy metals and emerging pollutants such as dyes and organics, (ii) the decontamination and remediation of soils, and (iii) the reduction in the number of suspended solids of a particulate matter (PM) type in the atmosphere. Because nanotechnology offers new horizons in materials science, nanocomposite tunable polymers are also studied and presented as promising materials in the context of developing sustainable and integrated products in society to ensure quality of life. As a class of future smart materials, the natural polymers and their nanocomposites are obtained from renewable resources, which are inexpensive materials with high surface area, porosity, and high adsorption properties due to their various functional groups. The information gathered in this review paper is based on the publications in the field from the last two decades. The future perspectives of these fascinating materials should take into account the scale-up, the toxicity of nanoparticles, and the competition with food production, as well as the environmental regulations.

In order to apply the concepts that allow the transition from a linear to a circular economy, waste generators and/or processors must identify those variants that generate products that can be used as secondary raw materials, thus also respecting the actions governing sustainable development. This paper presents such a variant, the briquetting of waste with high iron content, waste generated on current flows in steel enterprises or deposited in industrial sites. The obtained briquettes are analyzed for chemical and mechanical characteristics so that can be used as secondary materials in the steel production. An optimization of the chemical composition using generic algorithms is also proposed in order to obtain the mechanical characteristics necessary for the proper handling of these products.

Materials used in the marine industry are exposed to extreme conditions, so it is necessary to meet remarkable characteristics, such as mechanical resistance, low density, and good corrosion resistance. The challenging environment requires continuous performance improvements, so this work is focused on developing new materials with superior properties, using the electrochemical deposition technique, which are convenient for marine engineering. High-entropy alloys have been attracting tremendous interest in many applications, due to their simple crystal structures and advantageous physical-chemical properties, such as high strength, anti-corrosion, erosion, and electro-magnetic capabilities. To identify the most appropriate compositions, MatCalc software was used to predict the structure and characteristics of the required materials, and thermodynamic and kinetic criteria calculations were performed. The modelling processes generated a series of optimal compositions in the AlCrCuFeNi alloy system, that are suitable to be used in anticorrosive and tribological applications. The composition and morphology of the obtained high entropy alloy thin films revealed a uniform structure, with a small grain profile. The corrosion resistance was investigated in artificial seawater to observe the behavior of the newly developed materials in demanding conditions, and the results showed improved results compared to the copper foil substrate.

Inconel 625 samples, obtained by Selective Laser Melting (SLM) and conventional technology, were tested for hot corrosion resistance against a molten mixture of Na₂SO₄ and V₂O₅. The assessments were performed in air, at 900 °C with exposure time of up to 96 h, and at 1000 °C for 8 h. Weight gain was higher for samples obtained by SLM, with 37.4% after 8 h, 3.98% after 24 h, 4.46% after 48 h, and 5.8% after 96 h at 900 °C (22.6% at 1000 °C, 8 h). Three stages of corrosion were observed, the first and last with a high corrosion rate, while the second one showed a slower corrosion rate. Corrosion behaviour depends on the morphology of the grain boundary, which can influence the infiltration of corrosive salts, and on the formation of Cr₂NiO₄ compound, which acts as a temporary barrier.

A cellular concrete with a fine porous structure was experimentally made using the corrosion technique for aluminum powder as an expanding agent in an aqueous solution of Ca(OH)₂. The originality of this paper was the use of our own production method for the fine aluminum powder through atomizing the recycled molten waste of this metal using concentrated jets of nitrogen. Additionally, the waste melting technique involved our own microwave heating method. A high weight proportion of calcined gypsum (maximum 82.3%) represented the main concrete binder. Using moderate contents of coal fly ash (3.6–11.1%) together with perlite (4.6–6.4%) to reduce the pore size and silica fume (0.3–1.2%) with pozzolanic properties, the aim was to obtain a macrostructure characterized by a very low pore size and to increase the compressive strength (by up to 4.1 MPa), despite the relatively low density (below 641 kg/m³). An industrial method of increasing the mechanical strength by steam curing fresh concrete was applied.

A glass foam with good thermal insulation characteristics (apparent density of 0.38 g/cm³, porosity of 81.9% and thermal conductivity of 0.089 W/m·K), high compressive strength (3.9 MPa) and a satisfactory microstructural homogeneity with pore size between 0.6–1.0 mm was obtained by sintering at 927 °C of flat glass waste, a glass waste usually not used in the manufacture of glass foam. The manufacturing recipe has been improved by the simultaneous use of two microwave susceptible foaming agents (SiC and Si₃N₄) and the addition of coal fly ash and an oxygen-supplying agent (MnO₂). The originality of the work was the simultaneous use of the two foaming agents and also the application of the technique of predominantly direct microwave heating, compared to the conventional heating methods commonly used in the manufacture of glass foam. The remarkable energy efficiency of the microwave heating technique led to high average heating rates without affecting the structural homogeneity and very low specific energy consumption.