The problem of nitrogen pickup in the smelting process of the electric arc furnace (EAF) has not been solved well. Using seven slag–steel equilibrium experiments and theoretical analysis, the relation of the foaming index and optical basicity with the nitrogen capacity of slag was clarified. Meanwhile, the effect of slag composition on the equilibrium distribution ratio of nitrogen and the mass transfer coefficient of nitrogen pickup was also studied. The results show that, with the increase in slag basicity, the nitrogen pickup amount, nitrogen pickup rate, and nitrogen equilibrium distribution ratio L_N increase. Increasing the foaming index of slag and reducing its optical basicity will increase the nitrogen capacity of slag, which is conducive to hindering the nitrogen pickup of molten steel. The relationship between slag optical basicity and nitrogen capacity can be expressed as lgC_N = −5.59lgΛ − 12.41. With the increase in the Al₂O₃ content of slag, the nitrogen pickup amount of molten steel decreases and the nitrogen pickup rate decreases. The test with MgO = 7.5% showed the highest nitrogen pickup rate and the highest nitrogen pickup mass transfer coefficient, which were 0.21 × 10⁻⁴%/min and 1.97 × 10⁻⁴ cm/s, respectively. The test with Al₂O₃ = 7.5% in slag showed the lowest nitrogen pickup rate and the lowest nitrogen pickup mass transfer coefficient, which were 0.08 × 10⁻⁴%/min and 1.35 × 10⁻⁴ cm/s, respectively.

Deoxidation of liquid steel is a key link that affects the quality of environmentally friendly free-cutting steel. The selection and addition sequence of deoxidizer affects the composition, size, distribution, and morphology of non-metallic inclusions, which ultimately affect the machinability of free-cutting steel. The effects of deoxidation processes on inclusions in environmentally friendly free-cutting steel were studied by high-temperature experiments and thermodynamic calculations. The content of total oxygen and inclusion characteristics in steel were analyzed by an oxygen and nitrogen analyzer, a metallographic microscope, a scanning electron microscope, and an energy spectrum analyzer. The results show that the inclusions in the process of an initial Si-Fe alloy addition followed by a manganese addition (H1) are mainly Al₂O₃-SiO₂-MnO composite inclusions in the liquid phase. In addition to the liquid phase Al₂O₃-SiO₂-MnO complex inclusions in the MnO-rich region, there are also some solid phase Al₂O₃-MnO inclusions with high Al₂O₃ content in the process of an initial manganese addition followed by a Si-Fe alloy addition (H2). In the two deoxidation experiments, Bi particles mainly exist in the form of adhesion to MnS inclusions. Referring to H2, the average value and median of the aspect ratio is larger and the number of sulfide inclusions with aspect ratio greater than 1.0 increases significantly in H1. In addition, the spheroidization degree of MnS inclusions in the H2 is relatively good.