The aim of the present paper is to apply the laser powder bed fusion process to a new biodegradable Mg-Zn-Zr-Ca alloy powder prepared via a mechanical alloying method from powder pure components. This additive manufacturing method is expected to allow for the obtaining of high biomechanical and biochemical performance. Various processing parameters for laser powder bed fusion are tested, with a special focus on laser energy density—E [J/mm³]—which is calculated for all experiment variants, and which represents an important processing parameter, dependent upon all the rest. The goal of all the trials is to find the most efficient schema for the production of small biodegradable parts for the medical domain, meaning the selection of optimal processing parameters. An important observation is that the most robust and homogeneous samples without cracks are obtained for lower values of the E, around 100 J/mm³. Thus, the most performant samples are analyzed by scanning electron microscopy, X-ray diffraction and by compression mechanical test.

The aim of the present paper is to apply the mechanical alloying process to obtain from powder components a new biodegradable Mg-based alloy powder from the system Mg-xZn-Zr-Ca, with high biomechanical and biochemical performance. Various processing parameters for mechanical alloying have been experimented with the ultimate goal to establish an efficient processing route for the production of small biodegradable parts for the medical domain. It has been observed that for the same milling parameters, the composition of the powders has influenced the powder size and shape. On the other hand, for the same composition, the highest experimented milling speed and time conduct to finer powder particles, almost round-shaped, without pores or various inclusions. The most uniform size has been obtained for the powder sample with 10 wt.%Zn. These powders were finally processed by selective laser melting, an additive manufacturing technology, to obtain a homogeneous experimental sample, without cracking, for future more systematical trials.

A new Mg-Zn-Zr-Ca alloy in a powder state, intended to be used for custom shaped implants, was obtained via a mechanical alloying method from pure elemental powder. Further, the obtained powder alloy was processed by a PBF-LB/M (powder bed fusion with laser beam/of metal) procedure to obtain additive manufactured samples for small biodegradable implants. A series of microstructural, mechanical and corrosion analyses were performed. The SEM (scanning electron microscopy) analysis of the powder alloy revealed a good dimensional homogeneity, with a uniform colour, no agglutination and almost rounded particles, suitable for the powder bed fusion procedure. Further, the PBF-LB/M samples revealed a robust and unbreakable morphology, with a suitable porosity (that can reproduce that of cortical bone) and without an undesirable balling effect. The tested Young’s modulus of the PBF-LB/M samples, which was 42 GPa, is close to that of cortical bone, 30 GPa. The corrosion tests that were performed in PBS (Phosphate-buffered saline) solution, with three different pH values, show that the corrosion parameters have a satisfactory evolution comparative to the commercial ZK 60 alloy.

A new Mg-Zn-Zr-Ca alloy in powder state was obtained via mechanical alloying method, from pure elemental powder. Further, the obtained powder-alloy was processed by selective laser melting (SLM) procedure to obtain 3D printed samples for small biodegradable implants. A series of microstructural, mechanical and corrosion analysis were performed. The SEM analysis of powder-alloy reveal a good dimensional homogeneity, with uniform colored, no agglutinated and almost rounded particles, suitable for selective laser melting procedure. Further, the SLM samples reveal a robust and unbreakable morphology, with a suitable porosity and without undesirable balling effect. The tested Young’s modulus of the SLM samples, of 42 GPa, is close to cortical bone one, of 30 GPa. The corrosion tests performed in PBS (Phosphate-buffered saline) solution show that the corrosion parameters have a satisfactory evolution.