Biomass chemical looping gasification (BCLG) is a promising autothermic route for producing sustainable, N₂-free, and carbon neutral syngas for producing liquid biofuels or high value hydrocarbons. However, different ash-related issues, such as high-temperature corrosion, fouling and slagging, bed agglomeration, or poisoning of the oxygen carrier might cause significant ecologic and economic challenges for reliable implementation of BCLG. In this work, lab-scale investigations under gasification-like conditions at 950 °C and thermodynamic modelling were combined for assessing the influence of composition, pre-treatment methods, such as torrefaction and water-leaching, and Ca-based additives on the release and fate of volatile inorganics, as well as on ash melting behavior. A deep characterization of both (non-)condensable gas species and ash composition behavior, joint with thermodynamic modelling has shown that different pre-treatment methods and/or Ca-additives can significantly counteract the above-mentioned problems. It can be concluded that torrefaction alone is not suitable to obtain the desired effects in terms of ash melting behavior or release of problematic volatile species. However, very promising results were achieved when torrefied or water-leached wheat straw was blended with 2 wt% CaCO₃, since ash melting behavior was improved up to a similar level than woody biomass. Generally, both torrefaction and water-leaching reduced the amount of chlorine significantly.

Biomass chemical looping gasification (BCLG) is a promising key technology for producing carbon neutral liquid biofuels.

The release of alkali metals (K, Na) and nonmetals (S, Cl) during a calcium looping (CaL) gasification process of waste derived-hydrochars, water-leached samples, and CaO-biomass blends was investigated. Special attention was paid to biomasses that are not particularly promising for gasification requirements but have a large occurrence in Europe, including Grape Bagasse, Organic Fraction of Municipal Solid Waste (OFMSW), Green Waste, and Out-of-use woods from construction debris and discarded furniture. The release experiments were performed at 650 °C in a flow channel reactor to investigate the behavior of inorganic trace substances. Hot-gas analysis was performed by Molecular Beam Mass Spectrometry (MBMS). Thermodynamic equilibrium calculations via FactSage indicate H₂S, carbonyl sulfide (COS), KCl, NaCl, and HCl as the main inorganic impurities. Thus, the focus of the experiments was placed on these species. It was found that the concentrations of trace elements released during gasification at 650 °C, such as H₂S, SO₂, KCl, and NaCl, are hardly affected by intense water-leaching. In contrast, carbonaceous materials from hydrothermal carbonization exhibit a higher concentration of trace potassium substances (K, KCl, and K₂Cl⁺). When biomass samples are combined with CaO, the total amount of inorganic trace compounds (K, Na, and S compounds) in the resulting syngas could be decreased.