With the continuous exploration and development of oil and gas resources to deep formations, the key treatment agents of water-based drilling fluids face severe challenges from high temperatures and salinity, and the development of high temperature and salt resistance filtration reducers has always been the focus of research in the field of oilfield chemistry. In this study, a nano-silica-modified co-polymer (NS-ANAD) gel was synthesized by using acrylamide, isopropylacrylamide, 2-acrylamide-2-methyl propane sulfonic acid, diallyl dimethyl ammonium chloride, and double-bond-modified inorganic silica particles (KH570-SiO₂) through free radical co-polymerization. The introduction of nanotechnology enhances the polymer’s resistance to high temperature degradation, making it useful as a high-temperature-resistant fluid loss reducer. Moreover, the anions (sulfonates) and cations (quaternary ammonium) enhance the extension of the polymer and the adsorption on the surface of bentonite particles in a saline environment, which in turn improves the salt resistance of the polymer. The drilling fluids containing 2.0 wt% NS-ANAD co-polymer gels still show excellent rheological and filtration performance, even after aging in high temperature (200 °C) and high salinity (saturated salt) environments, showing great potential for application in deep and ultra-deep drilling engineering.

With increasing global energy consumption, oil/gas drilling has gradually expanded from conventional shallow reservoirs to deep and ultra-deep reservoirs. However, the harsh geological features including high temperature and high salinity in ultra-deep reservoirs have become a critical challenge faced by water-based drilling fluids (WDFs), which seriously deteriorate the rheology and fluid loss properties, causing drilling accidents, such as wellbore instability and formation collapse. In this study, a novel temperature- and salt-resistant micro-crosslinked polyampholyte gel was synthesized using N,N-dimethylacrylamide, diallyldimethyl ammonium chloride, 2-acrylamido-2-methylpropanesulfonic acid, maleic anhydride and chemical crosslinking agent triallylamine through free radical copolymerization. Due to the synergistic effect of covalent micro-crosslinking and the reverse polyelectrolyte effect of amphoteric polymers, the copolymer-based drilling fluids exhibit outstanding rheological and filtration properties even after aging at high temperatures (up to 200 °C) and high salinity (saturated salt) environments. In addition, the zeta potential and particle size distribution of copolymer-based drilling fluids further confirmed that the copolymer can greatly improve the stability of the base fluid suspension, which is important for reducing the fluid-loss volume of WDFs. Therefore, this work will point out a new direction for the development of temperature- and salt-resistant drilling fluid treatment agents.

During the exploitation of deep and ultradeep oil and gas resources, the high-temperature problem of deep reservoirs has become a major challenge for water-based drilling fluids. In this study, a novel high-temperature-resistant filtrate reducer (LDMS) with low molecular weight was synthesized using N, N-dimethylacrylamide; sodium p-styrene sulfonate; and maleic anhydride, which can maintain the performance of a drilling fluid gel system under high temperature. Unlike the conventional high-temperature-resistant polymer filtrate reducer, LDMS does not significantly increase the viscosity and yield point of the drilling fluid gel systems. After aging at 210 °C, the filtrate volume of a drilling fluid with 2 wt% LDMS was only 8.0 mL. The mechanism of LDMS was studied by particle size distribution of a drilling fluid gel system, Zeta potential change, adsorption experiment, change of bentonite interlayer spacing, filter cake scanning electron microscope, and related theoretical analysis. The mechanism study revealed that LDMS could be adsorbed on the surface of bentonite particles in large quantities and intercalated into the interlayer of bentonite. Thus, it can improve the hydration degree of bentonite particles and the colloidal stability of the drilling fluid gel system, maintain the content of fine particles in the drilling fluid gel system, form a compact mud cake, and significantly reduce the filtrate volume of the drilling fluid gel system. Therefore, this work will promote the application of a low-molecular-weight polymer filtrate reducer in high-temperature-resistant water-based drilling fluid gel systems.

To develop high-salinity, high-temperature reservoirs, two hydrophobically associating polymers as fracturing fluid thickener were respectively synthesized through aqueous solution polymerization with acrylamide (AM), acrylic acid (AA), 2-acrylamido-2-methylpropanesulfonic acid (AMPS), nonionic polymerizable surfactant (NPS) and double-tail hydrophobic monomer (DHM). The thickener ASDM (AM/AA/AMPS/NPS/DHM) and thickener ASD (AM/AA/AMPS/DHM) were compared in terms of properties of water dissolution, thickening ability, rheological behavior and sand-carrying. The results showed that ASDM could be quickly diluted in water within 6 min, 66.7% less than that of ASD. ASDM exhibited salt-thickening performance, and the apparent viscosity of 0.5 wt% ASDM reached 175.9 mPa·s in 100,000 mg/L brine, 100.6% higher than that of ASD. The viscosity of 0.5 wt% ASDM was 85.9 mPa·s after shearing for 120 min at 120 °C and at 170 s⁻¹, 46.6% higher than that of ASD. ASDM exhibited better performance in thickening ability, viscoelasticity, shear recovery, thixotropy and sand-carrying than ASD. The synergistic effect of hydrophobic association and linear entanglement greatly enhancing the performance of ASDM and the compactness of the spatial network structure of the ASDM was enhanced. In general, ASDM exhibited great potential for application in extreme environmental conditions with high salt and high temperatures.

To overcome the problems of long dissolution time and high investment in surface facilities of powder thickeners in hydraulic fracturing, a novel suspension of a thickener as a fracturing fluid was prepared using powder polyacrylamide, nano-silica, and polyethylene glycol by high-speed mixing. The suspension and powder were compared in terms of properties of solubility, rheological behavior, sand carrying, drag reduction, and gel breaking. The results showed that the suspension could be quickly diluted in brine within 5 min, whereas the dissolution time of powder was 120 min. The suspension exhibited better performance in salt resistance, temperature resistance, shear resistance, viscoelasticity, sand carrying, and drag reduction than powder. The powder solution was broken more easily and had a lower viscosity than suspension diluent. These improvements in properties of the suspension were due to the dispersion of nano-silica in the polymer matrix; the mobility of thickener chains was inhibited by the steric hindrance of the nano-silica. Nano-silica particles acted as crosslinkers by attaching thickener chains, which strengthened the network structure of the thickener solution. The presence of hydrogen bonds between the thickener matrix and the nano-silica restricted the local movement of thickener chains, leading to a stronger spatial network. Therefore, this novel suspension showed good potential for fracturing applications.