During the exploitation of deep and ultradeep oil and gas resources, the high-temperature problem of deep reservoirs has become a major challenge for water-based drilling fluids. In this study, a novel high-temperature-resistant filtrate reducer (LDMS) with low molecular weight was synthesized using N, N-dimethylacrylamide; sodium p-styrene sulfonate; and maleic anhydride, which can maintain the performance of a drilling fluid gel system under high temperature. Unlike the conventional high-temperature-resistant polymer filtrate reducer, LDMS does not significantly increase the viscosity and yield point of the drilling fluid gel systems. After aging at 210 °C, the filtrate volume of a drilling fluid with 2 wt% LDMS was only 8.0 mL. The mechanism of LDMS was studied by particle size distribution of a drilling fluid gel system, Zeta potential change, adsorption experiment, change of bentonite interlayer spacing, filter cake scanning electron microscope, and related theoretical analysis. The mechanism study revealed that LDMS could be adsorbed on the surface of bentonite particles in large quantities and intercalated into the interlayer of bentonite. Thus, it can improve the hydration degree of bentonite particles and the colloidal stability of the drilling fluid gel system, maintain the content of fine particles in the drilling fluid gel system, form a compact mud cake, and significantly reduce the filtrate volume of the drilling fluid gel system. Therefore, this work will promote the application of a low-molecular-weight polymer filtrate reducer in high-temperature-resistant water-based drilling fluid gel systems.

In drilling deep complex formations, most drilling fluid additives have insufficient temperature and salt tolerance, resulting in the decline of drilling fluid performance. This study used 2-acrylamide-2-methylpropane sulfonic acid, acrylamide, dimethyl diallyl ammonium chloride and modified nano-laponite to synthesize a nanocomposite filtrate reducer (ANDP) with excellent temperature and salt resistance, which can maintain the performance of drilling fluid. The structure of ANDP was analysed by a transmission electron microscope and an infrared spectrometer. The thermal stability of ANDP was studied by thermogravimetric analysis. The performance of ANDP was evaluated in a water-based drilling fluid. The mechanism was analysed per clay particle size distribution, Zeta potential, filter cake permeability and scanning electron microscopy imaging. The results show that ANDP has good thermal stability and the expected molecular structure. The filtration of freshwater drilling fluid after ageing at 200°C is 10.4 ml and that of saturated brine drilling fluid is 6.4 ml after ageing at 150°C. Mechanism analysis suggests that the ANDP increases the thickness of clay particle hydration layer and maintains the colloidal stability of the drilling fluid. ANDP inhibits the agglomeration of clay particles and significantly reduces the filtration by forming dense mud cake.

An inhibitor that can effectively inhibit shale hydration is necessary for the safe and efficient development of shale gas. In this study, a novel ionic liquid copolymer shale inhibitor (PIL) was prepared by polymerizing the ionic liquid monomers 1-vinyl-3-aminopropylimidazolium bromide, acrylamide, and methacryloyloxyethyl trimethyl ammonium chloride. The chemical structure was characterized using fourier transform infrared spectroscopy (FT-IR) and hydrogen-nuclear magnetic resonance (H-NMR), and the inhibition performance was evaluated using the inhibition of slurrying test, bentonite flocculation test, linear expansion test, and rolling recovery test. The experimental results showed that bentonite had a linear expansion of 27.9% in 1 wt% PIL solution, 18% lower than that in the polyether amine inhibitor. The recovery rate of shale in 1 wt% PIL was 87.4%. The ionic liquid copolymer could work synergistically with the filtrate reducer, reducing filtration loss to 7.2 mL with the addition of 1%. Mechanism analysis showed that PIL adsorbed negatively charged clay particles through cationic groups, which reduced the electrostatic repulsion between particles. Thus, the stability of the bentonite gel systems was destroyed, and the hydration dispersion and expansion of bentonite were inhibited. PIL formed a hydrophobic film on the surface of clay and prevented water from entering into the interlayer of clay. In addition, PIL lowered the surface tension of water, which prevented the water from intruding into the rock under the action of capillary force. These are also the reasons for the superior suppression performance of PIL.