Atmospheric corrosion is one of the major sources of hydrogen in a high-strength-steel product in service. Even low concentrations of absorbed hydrogen can cause a hydrogen embrittlement-related material degradation. The extent of atmospheric corrosion and thus the related hydrogen entry is highly dependent on the environmental parameters, such as the relative humidity. The present work focused on the hydrogen entry at low relative humidity, where atmospheric corrosion rates are expected to be low. Hydrogen insertion and distribution in CP1000 steel induced by corrosion under dried and rewetted single droplets of aqueous NaCl and MgCl₂ solution were studied using the Scanning Kelvin Probe (SKP) and the resulting amounts of diffusible hydrogen were analyzed using thermal desorption mass spectrometry (TDMS). Corrosion product analyses were carried out with SEM/EDX, XRD, and Mössbauer spectroscopy. The results revealed the strong impact of salt type and concentration on the hydrogen entry into steel. The hygroscopic effect of MgCl₂ and the formed corrosion products were responsible for the prolonged insertion of hydrogen into the steel even at very low levels of relative humidity.