The thin film of N-doped ZnO/CNT nanocomposite was successfully fabricated on soda lime glass substrate by a simple sol-gel drop-coating method. The structural, morphological, chemical, and optical properties of as prepared samples were characterized by a variety of tools such as X-ray Diffraction (XRD), Field Emission Scanning Electron Microscopy (FE-SEM), Fourier Transform Infrared spectroscopy (FT-IR), and UV-visible spectroscopy. The hexagonal crystalline structure was confirmed from XRD measurement without any other impurity phase detection in samples. The N-doped ZnO/CNT composite showed excellent photo-catalytic activity towards cationic methylene blue (MB) dye degradation with 100% removal rate under UV light irradiation as compared to N-doped ZnO (65%) and pure ZnO (47.36%). The convincing performance has also been observed for the case of visible light irradiation. The enhancement of that photocatalytic activity might be due to narrowing the band gap as well as the reduction of electron–hole pair recombination in ZnO matrix with the incorporation of dopant nitrogen and CNT. It is assumed from the obtained results that N-doped ZnO/CNT nanocomposite thin film can be employed as an economically achievable and ecofriendly method to degrade dye with UV and visible light irradiation. Additionally, density functional theory (DFT) calculations were applied to explore the effect of N-doping on electronic structure of ZnO. The computational study has supported the experimental results of significant band gap contraction, which leads to the maximum absorption towards higher wavelength and no appreciable change of lattice parameters after doping. A conceivable photocatalytic mechanism of N-doped ZnO/CNT nanocomposite has been proposed as well.

Hydrogen bonding in polyurethane (PU) is imposed by molecular parameters. In this study, the effect of structural isomerism of certain monomers on hydrogen bonding of waterborne polyurethane (WBPU) was studied theoretically and experimentally. Two dihydroxybenzene (DHB)-based structural isomers such as catechol (CC) and hydroquinone (HQ), with different OH positions on the inner benzene core, had been used. Two series of WBPU dispersions were prepared using CC and HQ with defined contents. The binding energies between the catechol (CC)/hydroquinone (HQ) (respective OH group) and urethane/urea were calculated theoretically. By using a density functional theory (DFT) method, it was found that the largest binding energy between the urea and CC was higher than that of urea and HQ. The FT-IR analysis of synthesized polymer was also carried out to compare the results with the theoretical values. The CC-based polymers showed a stronger hydrogen bond both theoretically and experimentally than those for HQ-based polymers. The higher level of hydrogen bond was reflected in their properties of CC-based polymers. The adhesive strength, thermal stability, and hydrophobicity were higher for CC-based materials than those for HQ-based materials. The adhesive strength was increased 25% with the addition of 2.0 wt% CC content. This adhesive strength slightly deviated at a moderately high temperature of 80 °C.

This study investigates the effectiveness of kaolin and bentonite catalysts in improving liquid hydrocarbon yields during the pyrolysis of waste tires. Raw clay, nitric acid-treated clay, and mono- or bimetal-impregnated clay were used as catalysts in the pyrolysis of waste tire. Acid-treated kaolin produced a higher yield of liquid hydrocarbons (43.24-47%) compared to acid-treated bentonite (35.34-41.85%). This improvement in the liquid yield can be attributed to the higher specific surface area and pore diameter of the acid-treated clay in comparison to raw kaolin (39.48%) and raw bentonite (31.62%). Moreover, the use of metal-impregnated catalysts, such as Fe/kaolin and Ni/Fe/kaolin, resulted in higher liquid yields (47%) compared to the 3 M HNO₃-treated kaolin catalyst (43.24%). Gas chromatography-mass spectrometry (GC-MS) analysis confirmed the presence of limonene, a crucial ingredient for commercial perfume production, in the liquid products. The calorific values of oil obtained through kaolin and bentonite catalysis were measured at 13,922 and 10,174 kcal/kg, respectively, further highlighting the potential of these catalysts in waste tire valorization.