According to literature data, different micro- and nanopowders have been used as a partial substitute for cement mortar due to their small size and large specific surface area. The aim of the work is to develop innovative materials based on cement mortar with antibacterial and self-cleaning properties, which can be used in the long-term maintenance of clean spaces. First, zinc oxide/hydroxyapatite (ZnO/Hap) powder denoted as ZH was synthesized by the hydrothermal method; then it was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM)/ energy dispersive spectroscopy (EDS), and adsorption–desorption isotherms. The second step was the cement mortar preparation: one plain, denoted E, and one with ZH powder inside, denoted MZH. Both mortars were subjected to self-cleaning and antibacterial tests. In the self-cleaning tests, two concentrated solutions of rhodamine B and methylene blue were used. MZH showed a better decolorating after 24 h of UV light than plain cement mortar denoted E for both solutions. In order to highlight the antibacterial effect of cement mortars on some strains of Gram-positive and Gram-negative bacteria, the direct contact method was used. The study revealed that, after 24 h of incubation, the planktonic growth of the E. coli strain is significantly inhibited in the presence of the MZH sample, compared to the control strain. MZH cement mortar exhibits a better growth inhibitory property than the plain cement mortar E.

This study investigates the additive manufacturing of 3D porous scaffolds based on walstromite-type silicate ceramics for bone tissue engineering applications. Walstromite powders were synthesized using the sol-gel method and printed using extrusion-based 3D printing. Both sintered and unsintered scaffolds were characterized using scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), X-Ray diffraction (XRD) and energy dispersive X-ray spectroscopy (EDS) analyses to evaluate the effects of sintering on microstructure, porosity, and mechanical properties. Results indicate that the unsintered scaffolds exhibited significantly higher compressive strength due to the presence of organic binders, whereas the sintered scaffolds demonstrated enhanced porosity, facilitating cell infiltration and nutrient flow. Therefore, the sintering process reduced compressive strength, probably due to the loss of organic compounds and increased porosity. These findings underline the need for optimizing sintering parameters to balance mechanical integrity and porosity, ensuring that the scaffolds meet the mechanical and biological requirements for bone regeneration. Alternative sintering methods, such as microwave sintering, are also suggested for future research to minimize the mechanical degradation observed post-sintering.