This study investigated the production of Cu²⁺-doped CoFe₂O₄ nanoparticles (CFO NPs) using a facile sol−gel technique. The impact of Cu²⁺ doping on the lattice parameters, morphology, optical properties, and electrical properties of CFO NPs was investigated for applications in electrical devices. The XRD analysis revealed the formation of spinel-phased crystalline structures of the specimens with no impurity phases. The average grain size, lattice constant, cell volume, and porosity were measured in the range of 4.55–7.07 nm, 8.1770–8.1097 Å, 546.7414–533.3525 ų, and 8.77–6.93%, respectively. The SEM analysis revealed a change in morphology of the specimens with a rise in Cu²⁺ content. The particles started gaining a defined shape and size with a rise in Cu²⁺ doping. The Cu_0.12Co_0.88Fe₂O₄ NPs revealed clear grain boundaries with the least agglomeration. The energy band gap declined from 3.98 eV to 3.21 eV with a shift in Cu²⁺ concentration from 0.4 to 0.12. The electrical studies showed that doping a trace amount of Cu²⁺ improved the electrical properties of the CFO NPs without producing any structural distortions. The conductivity of the Cu²⁺-doped CFO NPs increased from 6.66 × 10⁻¹⁰ to 5.26 × 10⁻⁶ ℧ cm⁻¹ with a rise in Cu²⁺ concentration. The improved structural and electrical characteristics of the prepared Cu²⁺-doped CFO NPs made them a suitable candidate for electrical devices, diodes, and sensor technology applications.

This research work employs a sol–gel process to prepare Ni _{1− x} Ce _x Fe ₂ O ₄ ( x = 0.00, 0.05, and 0.10) samples.