The present study is a detailed literal survey on the bond behavior of FRP (Fiber Reinforced Polymer) reinforcing bars embedded in concrete. There is an urgent need for the accurate assessment of the parameters affecting the FRP–concrete bond and quantification of these effects. A significant majority of the previous studies could not derive precise and comprehensive conclusions on the effects of each of these parameters. The present study aimed at listing all of the physical parameters affecting the concrete-FRP bond, presenting the effects of each of these parameters based on the common opinions of the previous researchers and giving reasonable justifications on these effects. The studies on each of the parameters are presented in detailed tables. Among all listed parameters, the surface texture was established to have the most pronounced effect on the FRP–concrete bond strength. The bond strength values of the bars with coarse sand-coating exceeded the respective values of the fine sand-coated ones. However, increasing the concrete strength was found to result in a greater improvement in bond behavior of fine sand-coated bars due to the penetration of concrete particles into the fine sand-coating layer. The effects of fiber type, bar diameter and concrete compressive strength on the bar bond strength was shown to primarily originate from the relative slip of fibers inside the resin of the bar, also known as the shear lag effect.

In this research, the mechanical properties of lightweight mortars containing different percentages of additional powder materials has been investigated using response surface methodology (RSM). Box–Behnken design, one of the RSM techniques, was used to study the effects of silica fume content (5, 10, and 15%), vermiculite/cement (V/C) ratio (4, 6, and 8), and temperature (300, 600, and 900 °C) on the ultrasonic pulse velocity (UPV), bending strength, and compressive strength of lightweight mortars. Design expert statistical software was accustomed to determining and evaluating the mix-design of materials in mortar mixtures and temperature effect on mortars. After preliminary experimental research of the relationships between independent and response variables, regression models were built. During the selection of the model parameters, F value, p-value, and R² values of the statistical models were taken into account by using the backward elimination technique. The results showed a high correlation between the variables and responses. Multi-objective optimization results showed that the critical temperatures for different levels of silica fume (5–10–15%) were obtained as 371.6 °C, 306.3 °C, and 436 °C, respectively, when the V/C ratio kept constant as 4. According to the results obtained at high desirability levels, it is found that the UPS values varied in the range of 2480–2737 m/s, flexural strength of 3.13–3.81 MPa, and compressive strength of 9.9–11.5 MPa at these critical temperatures. As a result of this research, RSM is highly recommended to evaluate mechanical properties where concrete includes some additional powder materials and was exposed to high temperature.