The aim of this clinical case study was to observe biopsy tissues at 5 months after an autograft of a partially demineralized dentin/cementum matrix (pDDM) into a tooth-extracted socket exhibiting healing failure. A 66-year-old female presented with healing failure in the cavity for 2 months after the extraction (#36). Initial X-ray photos showed a clear remainder of lamina dura (#36), a residual root (#37), and a horizontal impaction (#38). The vital tooth (#38) was selected for pDDM. The third molar crushed by electric mill was decalcified in 1.0 L of 2.0% HNO₃ for 20 min and rinsed in cold distilled water. The pDDM granules (size: 0.5–2.0 mm) were grafted immediately into the treated socket. X-ray views just after pDDM graft showed radio-opaque granules. At 5 months after pDDM graft, the surface of regenerated bone was harmonized with the mandibular line, and bone-like radio-opacity was found in the graft region. The biopsy tissue (diameter: 3.0 mm) at 5 months after pDDM graft showed that mature bone was interconnected with the remaining pDDM. The novel histological evidence highlighted that newly formed bone was connected directly with both dentin-area and cementum-area matrix of pDDM. We concluded that pDDM contributed to the regeneration of bone in the unhealed socket, and this regeneration prepared the socket for implant placement. Autogenous pDDM could be immediately recycled as an innovative biomaterial for local bone regeneration.

Vertical augmentation is one of the most challenging techniques in bone engineering. Several parameters, such mechano-chemical characteristics, are important to optimize vertical bone regeneration using biomaterials. The aims of this study were to chemically characterize human dentin blocks (calcified demineralized dentin matrix: CDM, partially demineralized dentin matrix: PDDM and completely demineralized dentin matrix: CDDM) (2 × 2 × 1 mm³) chemically and evaluate the behavior of PDDM blocks on non-scratched or scratched skulls without periosteum of adult rats (10–12 months old, female) as a vertical augmentation model. The dissolved efficiency of CDM showed 32.3% after ultrasonic demineralization in 1.0 L of 2% HNO₃ for 30 min. The 30 min-demineralized dentin was named PDDM. The SEM images of PDDM showed the opening of dentinal tubes, nano-microcracks and the smooth surface. In the collagenase digestion test, the weight-decreasing rates of CDM, PDDM and CDDM were 9.2%, 25.5% and 78.3% at 12 weeks, respectively. CDM inhibited the collagenase digestion, compared with PDDM and CDDM. In the PDDM onlay graft on an ultrasonically scratched skull, the bone marrow-space opening from original bone was found in the bony bridge formation between the human PDDM block and dense skull of adult senior rats at 4 and 8 weeks. On the other hand, in the cases of the marrow-space closing in both non-scratched skulls and scratched skulls, the bony bridge was not formed. The results indicated that the ultrasonic scratching into the compact parietal bone might contribute greatly to the marrow-space opening from skull and the supply of marrow cells, and then bony bridge formation could occur in the vertical augmentation model without a periosteum.

Vertical and horizontal bone augmentation is one of the most challenging techniques in bone engineering. The use of barrier membranes and scaffolds in guided bone regeneration (GBR) procedures is a common approach for the treatment of lost bone around teeth and dental implants. The aim of this study was to estimate the barrier effects of a synthetic poly (lactic acid/caprolactone) [P(PA/CL)] bilayer membrane for GBR, compared to a porcine collagen bilayer membrane, in the vertical augmentation model on 10–12-months old rat skull without periosteum. The HAp block (diameter: 4 mm, height: 3 mm, porosity:75%, average pore size:150 μm) was placed on the rat skull without a periosteum. The P(LA/CL) membrane (solid layer: 25 μm, porous layer: 175 μm) or the collagen membrane (solid layer, porous layer) was applied onto the HAp block. At 3, 6, and 12 weeks after the surgery, the incised tissues were fixed, decalcified, and stained with hematoxylin and eosin for histological evaluation. The P(LA/CL) membrane remained until 12 weeks and could achieve barrier effects to inhibit cellular invasion from the repositioned soft tissues. Local bone formation occurred in the interconnected pores of HAp at 6 weeks. On the other hand, the collagen membrane did not inhibit cellular invasion for its expansion until 3 weeks, and was absorbed until 6 weeks. The results indicated that the P(LA/CL) membrane might be effective in GBR as occlusive absorbable membrane.