The very early stages of alkaline activation of slag control its rheology and setting, but also affect its hydration, which occurs later. Simultaneously, these parameters are dictated by the nature and dose of the alkaline activator. Therefore, we investigated and compared the changes in slag particles (SEM, BET, laser diffraction), as well as in the pore solution composition (ICP–OES), pH, and conductivity, of alkali-activated slag (AAS) pastes containing the three most common sodium activators (waterglass, hydroxide, and carbonate) and water during the first 24 h of its activation. To ensure the best possible comparability of the pastes, a fairly nontraditional mixture design was adopted, based on the same concentration of Na⁺ (4 mol/dm³) and the same volume fraction of slag in the paste (0.50). The results were correlated with the pastes’ hydration kinetics (isothermal calorimetry), structural build-up (oscillatory rheology), and setting times (Vicat). Great differences were observed in most of these properties, in the formation of hydration products, and in the composition of the pore solution for each activator. The results emphasize the role of the anionic groups in the activators and of the pH, which help predict the sample’s behavior based on its calorimetric curve, and offer data for further comparisons and for the modelling of AAS hydration for specific activators.

Belite-rich cement is a low carbon footprint binder. However, its use is accompanied by a low initial rate of hydration. This can be partially eliminated by grinding to a high specific surface or through the addition of admixtures (mineralizators or activators). The influence of alkaline activators CaSO₄, Na₂SO₄ and Na₂CO₃ (in the amount of 5 wt.% related to the clinker weight) on the hydration course, as well as the quantity of hydration products in belite-rich cements, were investigated in this paper. Belite-rich clinker was laboratory-synthetized and ground together with activators to prepare various belite-rich cements. Next, the hydration kinetics and the hydrated phase assemblage were investigated using isothermal calorimetry, X-ray powder diffraction and thermogravimetric and differential thermal analyses. The use of selected admixtures allowed us to obtain belite-rich cements with higher hydraulic activity in the initial period.