The aim of the present paper is to investigate an innovative high corrosion resistance coating realized by electrospark deposition. The coating material was fabricated from HfNbTaTiZr high-entropy alloy. HEA was produced by the mechanical alloying of Hf, Nb, Ta, Ti, and Zr high-purity powders in a planetary ball mill, achieving a good homogenization and a high alloying degree, followed by spark plasma sintering consolidation. The electrodes for electrospark deposition were cut and machined from the bulk material. Stainless steel specimens were coated and electrochemically tested for corrosion resistance in a 3.5% NaCl saline solution.

High-entropy alloys (HEAs) gained interest in the field of biomedical applications due to their unique effects and to the combination of the properties of the constituent elements. In addition to the required property of biocompatibility, other requirements include properties such as mechanical resistance, bioactivity, sterility, stability, cost effectiveness, etc. For this paper, a biocompatible high-entropy alloy, defined as bio-HEA by the literature, can be considered as an alternative to the market-available materials due to their superior properties. According to the calculation of the valence electron concentration, a majority of body-centered cubic (BCC) phases were expected, resulting in properties such as high strength and plasticity for the studied alloy, confirmed by the XRD analysis. The tetragonal (TVC) phase was also identified, indicating that the presence of face-centered cubic (FCC) phases in the alloyed materials resulted in high ductility. Microstructural and compositional analyses revealed refined and uniform metallic powder particles, with a homogeneous distribution of the elemental particles observed from the mapping analyses, indicating that alloying had occurred. The technological characterization of the high-entropy alloy-elaborated powder revealed the particle dimension reduction due to the welding and fracturing process that occurs during mechanical alloying, with a calculated average particle size of 45.12 µm.

The aim of this paper is to establish the cost-effectiveness of high-entropy alloy coatings, using the electrospark deposition technique, designed for a geothermal turbine blade’s leading edge. The deposition of materials with high resistance to corrosion and erosion aims to increase the blade’s service life, reduce maintenance costs and improve production efficiency. According to our previous research on the CoCrFeNiMo_x high-entropy alloy system, the results showed a high corrosion resistance when in bulk or as a coating, and when tested in geothermal steam and in a saline solution. Based on the results, the high-entropy alloy was subjected to further analyses. The paper focused on two aspects of the research. The first direction was to explore the possibility of obtaining an effective, protective high-entropy alloy layer by the electrospark deposition method. To this end, various tests were performed to demonstrate that the new material possesses superior properties and is suitable for the geothermal environment’s demands. The second direction was to calculate the economic efficiency of coating the areas intensely subjected to wear, based on reports published by the geothermal power plants’ representatives. The final costs were compared with the commercially available equipment parts, and also with the general maintenance costs. From the calculation of the cost efficiency for the CoCrFeNiMo_0.85 high-entropy alloy, it resulted that the deposition method and the properties of the material are suitable for the operating conditions, representing an efficient and easy to apply solution to reduce maintenance costs in the geothermal industry.

The main objective of this study was to develop a high-entropy alloy (HEA) derived from the Co_xCrFeNiTi HEA system (x = 0.5, 1) for protective coatings using the magnetron sputtering method. In order to produce the high-entropy alloy targets required for the magnetron sputtering process, mechanically alloyed metallic powders were consolidated via spark plasma sintering (SPS). The microstructural analysis results of the HEA mixture presented morphology changes after 30 h of alloying, with the particles presenting uniform polygonal shapes and dimensions. Subsequently, 316L stainless steel (SS) specimens were coated via magnetron sputtering, comparing their composition with that of the sputtering targets used for deposition to establish stoichiometry. Microstructural analyses of the SPSed HEAs revealed no defects and indicated a uniform elemental distribution across the surface. Furthermore, the CoCrFeNiTi equiatomic alloy exhibited a nearly stoichiometric composition, both in the coating and the sputtering target. The XRD analysis results indicated that amorphous coatings were obtained for both Co_0.5CrFeNiTi and the CoCrFeNiTi HEA, and nanoindentation tests indicated that the CoCrFeNiTi HEA coating presented a hardness of 596 ± 22 HV, compared to the 570 ± 19 HV measured for Co_0.5CrFeNiTi, suggesting an improved wear resistance.

Mechanical alloying (MA) is a high-energy ball milling process results in the obtaining of simple and stable microstructures having increased homogeneity compared to other non-equilibrium synthesis methods. The aim of this paper was to develop a high entropy alloy with an improved hardness value suitable for coating turbine blades working in geothermal steam. CoCrFeNiMo high entropy alloy was processed in solid state, using mechanical alloying. After 40h milling time in a planetary ball mill the alloyed sample was consolidated using spark plasma sintering process. The samples obtained were investigated with the aid of optical and electron microscope, X ray diffraction and the hardness value was determined. The results obtained revealed that the powder was completely alloyed after 40 hour milling and the mixture between BCC and FCC phases resulted in 34% improved hardness value in comparison with a stainless steel usually used for turbine blades working in geothermal environment.