Rock mass, the heterogeneous natural material composed of rock and discontinuities, is an important part of engineering construction. Discontinuities affect the mechanical properties of natural rock mass and further threaten the stability of rock engineering. To study the failure characteristics of anchored structure plane with different JRC, jointed specimens with four different JRC were fabricated by pouring cement mortar. Specimens were tested under four different normal loads to figure out how JRC and anchorage angle affect the mechanical properties of anchored structure plane. Besides, acoustic emission (AE) testing technology was adopted to explore the AE characteristics of anchored structural plane under shearing. The results showed that there exists a positive correlation between the peak shear strength and JRC. The undulation shape of structural plane led to an obvious downward trend in the strain softening stage of the structural plane with JRC of 6–8 and 18–20. When the anchorage angle ranged from 45° to 60°, the potentiation of bolt was the most significant. Based on the AE results, the larger the normal stress, the more likely the cumulative count curves were to enter the fast growth phase before the peak. The characteristics of b-value curves are mainly related to the topography of structural planes and whether the bolt is deformed. In the direct shear test, the cumulative proportion of shear cracks was more than 85%, which is much higher than that of tensile cracks. The variation of cumulative tensile cracks goes through three stages: slow growth, rapid growth, and slow growth. Compared with the unanchored structural plane, the variation range of real-time tensile cracks of the anchored structural plane is large, and sometimes the proportion of real-time tensile cracks may reach 80%.

The existence of lead-zinc tailings threatens the social and ecological environment. The recycling of lead–zinc tailings is important for the all-round green transformation of economic society. In this study, the possibility of fabricating sintered ordinary bricks with lead–zinc tailings was studied based on orthogonal experimentation, and the phase composition and micromorphology of sintered products were analyzed by X-ray diffraction (XRD) and scanning electron microscope (SEM). With lead–zinc tailings as the main material, and clay and fly ash as additives, the effect of clay content, forming pressure, sintering temperature, and holding time on physical properties of sintered bricks was analyzed. The results show that clay content and sintering temperature have a major effect on compressive strength, while sintering temperature and holding time play an important role in water absorption. During sintering, mica, chlorite, and other components in lead–zinc tailings are decomposed to form albite, hematite, maghemite, and anhydrite, which play a role in the strength of bricks. The optimal process parameters were found to be a ratio of lead–zinc tailings:clay:fly ash = 6:3:1, forming pressure of 20 MPa, firing temperature of 1080 °C, and holding time of 60 min. The corresponding compressive strength and water absorption were 34.94 MPa and 16.02%, which meets the Chinese sintered ordinary bricks standard (GB/T 5101-2017).

Rock bridges are important structures for maintaining rock mass stability, but their shapes are not well known. The researchers propose a method for determining the shape of rock bridges based on experiments, discrete element methods and machine learning, which is applicable to complex joints with arbitrary spatial distribution. Numerical models are constructed using the discrete element method, and parameter matching is performed based on experimental results. The particles were clustered using the k-means algorithm with the maximum principal stress (σ₁) as an indicator and the selection of initial values was optimized. The density-based spatial clustering of applications with noise (DBSCAN) algorithm was used to delete the noise from the particles. Finally, the boundary lines of the particles were extracted by self-programming, and the shape of the rock bridges was determined. Twenty-four sets of simulations were used to analyze the effect of rock bridges on the specimens. The results show that the failure mode of the specimen changes from shear to tensile damage as the cohesive force of the rock bridges increases. The peak strength and peak strain of the specimens increased with the increase of cohesion in the rock bridge. Rock bridges are the fastest growing areas of stress in the specimen.

The accumulation of lead–zinc tailings will cause a series of problems, including geological disasters and environmental pollution. Efficient secondary utilization of lead–zinc tailings is crucial. In this study, the activity of lead–zinc tailings was stimulated by thermal activation. The optimal thermal activation parameters are a thermal activation temperature of 900 °C and a holding time of 30 min. Based on the response surface methodology, the effect of raw materials content on cementitious material strength was analyzed, and the relational model between cementitious material strength and experimental variables was established. The results show that the sensitivity order of cementitious material strength at 28 days curing age is sand/cement ratio > water/cement ratio > fly ash content > tailing content. According to the relational model, the optimal materials ratio is as follows: tailing/fly ash/cement = 28.99%:14.58%:56.43%, and the sand/binder ratio and water/binder ratio are 1:1 and 0.47, respectively. The corresponding cost is CNY 290.965 per ton, which is the lowest. The strength of cementitious material with these parameters can reach 20 MPa, which meets the requirements of “Technical specification for application of solid waste cementitious material (T/CECS 689-2020)”.

Under the condition of constant external stress, the displacement and stress of the joint will be adjusted continuously with time, resulting in the creep phenomenon, that is, the continuous increase of the strain with time, which further causes the damage of the jointed rock mass. In order to study the size effect of joint shear rheological mechanical properties, this paper conducted shear rheological numerical simulations on nonpenetrating and penetrating joint models established in Particle Flow Code (PFC) and analyzed the effect of specimen size on the rheological and shear mechanical behavior of the model. The results show the following: (1) For the rheological direct shear test, the instantaneous shear displacement of the joint increases continuously as the size increases, showing a significant positive size effect. (2) For through-type joints, only the cohesion shows a certain size effect, and the shear strength and friction angle have a nonobvious relation with specimen size. (3) For anchored through-type joints, the increase of the model size leads to a decrease in shear strength, while the friction angle-size effect of joints is not remarkable.