This study aims to investigate the comparative performance of ester- and ether-based polycarboxylate superplasticizers in maintaining the fluidity and controlling the setting time of alkali-activated slag (AAS) paste. The experiments employed rheological tests, mini-slump tests, ultrasonic pulse velocity (UPV) measurements, and gel permeation chromatography (GPC) analysis. The results indicate that ether-based superplasticizers maintain fluidity approximately 25% longer than their ester-based counterparts and extend the setting time by about 30%. The enhanced performance of ether-based superplasticizers is attributed to their superior molecular stability in highly alkaline environments, which mitigates early polymer degradation. Additionally, the Na₂O/SiO₂ ratio was maintained at 1:1 throughout the experiments to ensure consistency in the activation process. The relationship between fluidity loss and the onset of setting occurs more rapidly in AAS paste than in conventional cement-based systems. These findings provide valuable insights for the development of environmentally friendly construction materials by optimizing the use of superplasticizers in alkali-activated systems.

This study investigates the quality characteristics and healing performance of precast concrete incorporating self-healing technology, with the aim of supporting smart city implementation. To enhance the self-healing capabilities of concrete, hybrid self-healing capsules, combining solid capsules and liquid capsules, were utilized, and their applicability and practicality were assessed. The findings revealed that incorporating hybrid self-healing capsules into precast concrete resulted in a reduction in slump by up to 14% and air content by up to 9%. Furthermore, the addition of hybrid capsules led to a maximum reduction in compressive strength of 16% and flexural strength of 18% at 28 days, while demonstrating an increase in healing efficiency as the capsule content increased. The results also indicated that the use of hybrid capsules enhanced the healing efficiency by approximately 16%, 25%, and 32% for mixing ratios of 1%, 3%, and 5%, respectively, with the overall healing efficiency ranging between 75% and 90%. Additionally, the interaction between the hybrid capsules and natural healing mechanisms promoted crystal formation around cracks, thereby significantly improving the long-term durability of the concrete.

The purpose of this study is to investigate the healing performance of solid capsules made of cement as a basis for manufacturing self-healing capsules that can heal cracks in cementitious composites. The solid capsules were mixed with 5%, 10%, and 15% concentrations on the cement. The self-healing performance of cementitious composites with solid capsules was investigated through three evaluations. First, the mechanical strength-healing performance was evaluated through a re-loading test. Second, the durability-healing performance was evaluated through a permeability test. Finally, the crack-healing performance was examined by observing the crack widths. Through evaluation of the healing performance of the solid capsules, the healing performance of the compressive strength was found to be high when the capsule proportion was 10% and its size was within the range of 300 μm to 850 μm. Furthermore, the splitting tensile strength showed a high healing performance when the capsule proportion mixed was 15% and its size was 850 μm. In the case of the permeability test, a capsule size of 850 μm showed a healing effect greater than 95%. Cracks with a width of up to 200 μm tended to heal using capsules with a size of 600 μm to 850 μm.

In this study, the effect of tapioca starch (TP) on mortar was evaluated by incorporating TP into the mortar mixture. The evaluation involved analyzing the mortar’s quality characteristics, performance, and fundamental quality improvements. The addition of TP resulted in a decrease in flow, which was attributed to increased viscosity. Specifically, a 10% reduction in flow was observed with a 0.025% increase in TP content. After 28 days, the impact of TP on the compressive strength of the mortar remained consistent, regardless of the TP amount. However, within the first 3 days, higher TP content accelerated strength development, with early compressive strength increasing by up to 20% at a 0.050% TP level. Additionally, bond strength improved by approximately 60% at a 0.050% TP concentration, and final shrinkage was reduced by 5%.

This paper aims to reduce the quantity of cement used by up to 80% by utilizing industrial by-products. By reducing the amount of cement used, there is an effect of reducing CO₂ emissions during cement manufacturing. To reduce the amount of cement used, ground granulated blast-furnace slag (GGBF), fly-ash (FA), and calcium carbonate (CC) were used as substitute materials for cement. CC is a by-product, discharged by collecting CO₂ emitted from a coal-fired power plant and reacting with additives. The specific surface area and the average particle size of CC used are 12,239 cm²/g and 5.9 μm (D₅₀), respectively. The viscosity of pastes that contained GGFF and FA decreased by up to 51 and 49% respectively compared to the use of only cement (OPC) paste. However, paste using with CC increased up to 23% in relation to plain. As a result of measuring slump flow, segregation resistance ability, and filling ability to evaluate construction performance, slump flow was reduced by up to 3% (G40F10C30) in relation to plain concrete. Segregation resistance ability of fresh concrete using, GGBF (15, 30, and 45%), FA (10, 20, and 30%), CC (10, 20, and 30%), the time it takes for the slump flow to reach 500 mm, time it takes to through the V-funnel showed a decreasing tendency as the usage of FA increased. However, CC increased with increasing mixing ratio. This trend is, the viscosity increase when CC was mixed in terms of rheology. Filling ability of fresh concrete using GGBF (15, 30, and 45%), FA (10, 20, and 30%) and CC (10, 20, and 30%), the criteria were met, and the average increase was 16% and the maximum was 20% in relation to plain concrete. In the case of compressive strength, the compressive strength at 1 day was found to be an average of 5 MPa when 80% of the cementitious was substituted. At 3 days, at least 8 MPa was measured. The compressive strength at 28 days showed a tendency to decrease as the mixing rate of CC increased, but was measured to be at least 34 MPa. The relationship between compressive strength and splitting tensile strength or elastic modulus at 28 days satisfies the standard range.