This study examined the possibility of utilizing Tungsten Mine Tailings (TMT) as cement substitute for manufacturing Self-consolidating Concrete (SCC). Rheological properties of mortar mixed with TMT was evaluated using mortar viscometer and evaluation of SCC in the fresh state was examined by applying the standard presented by Japanese Society of Civil Engineering (JSCE). Its feature at hardening state was examined through compressive strength, splitting tensile strength, modulus of elasticity, carbonation depth and drying shrinkage test. As a result of examination, viscosity and yield stress decreased as the mixing ratio of TMT increased. Properties of SCC mixed with TMT while it is fresh state satisfied the standard within the mixing ratio of TMT at 20%. As for the mechanical properties of SCC, as the mixing ratio of TMT increased, the compressive strength decreased, carbonation depth and drying shrinkage rate increased. The relationship between the compression strength and the splitting tensile strength was found to be similar to the expression presented by CEB-FIP, and the relationship between the compression strength and the elastic moduli was found to be similar to the expression suggested by ACI 318-08 and CEB-FIP.

Self-healing cement composites are generally produced by using materials such as inorganic powders, bacteria pellets, and microcapsules. Among them, inorganic powder-type healing materials tend to decrease in healing performance over time because they react relatively quickly. Accordingly, this study encapsulated self-healing inorganic reactive powders in solid capsules (SC) in order to delay their reaction. The capsule surface was coated with a membrane to prevent moisture from permeating it. SC were utilized to provide the self-healing effect to the repair mortar. SC were mixed at three rates (0%, 5%, and 10%) by the binder mass of the repair mortar. The fundamental properties, including rheology, table flow, strength, and length change, and the self-healing performance of the self-healing repair mortar mixes were investigated. It was found that the rheological and mechanical properties of the repair mortar decreased slightly as the amount of SC increased. On the other hand, for a crack width of 0.25 mm and crack inducing age of 28 days, the healing performance of repair mortar specimens containing SC was at least 20 pt% better than that of plain repair mortar after a healing period of 28 days.

Advancements in material science have led to the development of various self-healing concrete technologies. Among these is the use of microcapsule-based self-healing materials. This study evaluated the effects of self-healing microcapsules on the quality and healing properties of mortar. A silicate-based inorganic material mixture was used as the healing material tested with ordinary Portland cement. Accordingly, the effects of microcapsules (MCs) on the rheological, mechanical, and healing properties of mortar were determined. The mixing of MCs reduced the plastic viscosity and yield stress of the cement composite material owing to the particle properties of the MCs. The reduction was in proportion to the mixing ratio. The evaluation results show that the unit water permeability decreased owing to the healing reaction immediately after crack initiation. The healing rate was more than 95% at 7 days of healing age when more than 3% of MCs was mixed. This study provides a reference for the optimal mixing rate of MCs to achieve an ideal concrete healing rate.

Recently, a self-healing technique capable of repairing cracks in structures has emerged. Among various self-healing technologies, self-healing capsules can be largely classified into two types, depending on the phase of the core material: solid capsules, in which the core material is a powder; and microcapsules, in which the core material is a liquid. Solid capsules and microcapsules have different mechanisms, and their capsule sizes are also distinctly different. This suggests that each has advantages and disadvantages. Most of the studies known to date have utilized single capsules. However, if one uses a mixture of the two types of capsules, it is possible to highlight the strengths of each capsule and compensate for the weaknesses. Therefore, in this study, the first research on complex capsules that mixed solid capsules and microcapsules was attempted. As a result of the experiment, the complex capsule slightly reduced the fluidity of the mortar, but the effect was not significant. Moreover, the complex capsule tended to reduce the compressive strength of the mortar. In particular, it was found that the effect of solid capsules on the reduction in compressive strength among complex capsules was greater than that of microcapsules. Conversely, the healing performance increased when the ratio of solid capsules in the complex capsules was large.

In the recent concrete industry, high-fluidity concrete is being widely used for the pouring of dense reinforced concrete. Normally, in the case of high-fluidity concrete, it includes high binder contents, so it is necessary to replace part of the cement through admixtures such as fly ash to procure economic feasibility and durability. This study shows the mechanical properties and field applicability of high-fluidity concrete using mass of fly ash as alternative materials of cement. The high-fluidity concrete mixed with 50% fly ash was measured to manufacture concrete that applies low water/binder ratio to measure the mechanical characteristics as compressive strength and elastic modulus. Also, in order to evaluate the field applicability, high-fluidity concrete containing high volume fly ash was evaluated for fluidity, compressive strength, heat of hydration, and drying shrinkage of concrete.