High-temperature resistant high-entropy alloys (HEAs) have attracted extensive attention due to their excellent thermodynamic stability and mechanical properties, especially at high temperatures. However, a highly effective method for large-size HEAs is still desirable but challengeable. This research reported a facile yet effective strategy for MoNbTaWTi HEAs via in-situ wire arc additive manufacturing (WAAM). The wire was MoNbTaWTi cable-type welding wire (CTWW) consisting of one center wire and seven twisted peripheral wires. Then, additive manufacturing of MoNbTaWTi high entropy alloys (HEAs) was accomplished, and various analytical techniques studied the microstructures and mechanical properties of the overlaying formed layers. X-ray diffraction showed the overlaying formed layers to contain a single disordered BCC solid solution phase with high-temperature structural stability. In addition, the single-phase BCC structure was maintained from 0 to 1400 °C. The bottom of the overlaying formed layers was made of columnar cellular structure, and the upper part resembled “cauliflower-like” fine dendrite and equiaxed crystal structure. The hardness of the overlaying formed layers averaged 533 HV_0.2 at room temperature. At 1000 °C, the hardness was around 110 HV₁, close to the value of Inconel 718 alloy (125 HV₁). The compressive strength of the overlaying formed alloy layers displayed no sensitivity towards change in temperature from 500 to 1000 °C. As the temperature rose from 500 to 1000 °C, the compressive strength changed from 629 to 602 MPa, equivalent to only a 27 MPa decrease. The latter was much higher than the strength of Inconel 718 alloy at the same temperature (200 MPa).

In order to explore the feasibility of underwater wet laser welding of the TC4 titanium alloy, research on the underwater laser self-fusion welding process was carried out. The weld structure and mechanical properties in both the air environment and the underwater environment were compared and analyzed. The results show that increasing the laser power and reducing the welding speed are beneficial to obtain a larger water depth threshold. Off-focus amount has little effect on water depth threshold; when the laser power is 3000 W and the welding speed is 5 mm/s, and the water depth exceeds 7 mm, a continuous weld cannot be formed. Compared with welding in the air, underwater welding has narrower weld width, smaller heat affected zone and finer crystal grains. The weld structure is mainly composed of α′ martensite and secondary acicular α′ phase, it is distributed in a net basket shape and the grain size at the top of the weld is finer. The hardness of the weld center is above 600 HV0.1, and the residual stress of the underwater welding weld is approximately symmetrically distributed. There is a large tensile stress along the welding direction at the weld, reaching 458 MPa. The larger residual tensile stress leads to the decrease of weld tensile strength, the tensile strength and elongation of the middle sample are only 52% and 77% of the base metal. Furthermore, the fracture mode is typical brittle fracture.

CoCrNi medium-entropy alloy has superior cryogenic properties with simultaneous growth of strength and plasticity at low temperatures. In order to observe the microstructure and deformation behavior of the alloy at the atomic scale, its mechanical properties and deformation mechanism at different temperatures and strain rates were investigated using molecular dynamics. It is indicated that the alloy’s strength was enhanced at low temperatures and high strain rates due to the production of high dislocation density. The introduction of grain boundaries significantly decreased the dislocation density during the alloy’s deformation and correspondingly reduced the crystal strength. However, the introduction of twin boundaries in polycrystalline grains obviously enhanced the strength of the polycrystal, especially at the twin boundary spacing of 3.08 nm. The strength’s enhancement was attributed to the increasing dislocation density produced by the interaction between twin boundaries and dislocations during deformation.

Arc welded 316 stainless steel coatings with flux-cored wires are very promising for marine service environments due to their low cost, high efficiency, and satisfactory performance, while they suffers from Cr dilution during the preparation process. Herein, based on the consideration of increasing the Cr content and ensuring the same value of the Cr/Ni equivalence ratio (Cr_eq/Ni_eq), 316-modified flux-cored wires, 316F (19Cr-12Ni-3Mo) and 316G (22Cr-14Ni-3Mo), were designed under the guidance of a Schaeffler diagram for the improvement of the electrochemical and mechanical properties of 316 stainless steel coatings. The designed flux-cored wires were welded into a three-layer cladding by the tungsten inert gas welding (TIG) process, and the microstructure, corrosion resistance, and mechanical properties of the claddings were investigated. The results showed that 316F and 316G consist of γ-Fe (austenite) and a small portion of δ-Fe (ferrite) as the Cr_eq/Ni_eq is approximately 1.5. However, due to the higher value of the equivalent Cr content (ECC), 316G has an additional intermetallic phase (σ), which precipitates as a strengthening phase at grain boundaries, significantly increasing the tensile and yield strength of 316G but reducing its plasticity. In addition, the corrosion current density (i_corr) and pitting potential (E_b) for 316G are 0.20447 μA·cm⁻² and 0.634 V, respectively, while the values for 316F are 0.32117 μA·cm⁻² and 0.603 V, respectively, indicating that 316G has better anti-corrosion performance.