Currently, the printed circuit boards (PCB) of waste electrical and electronic equipment (WEEE) are attracting interest among researchers for environmental concern reasons and mainly for their content of precious metals such as gold. Thus, this study aims to characterize different types of PCBs from mobile phones in relation to the amount of gold contained, to evaluate alternative leaching agents for the gold (ammonium and sodium thiosulfate) and compare these to commercial stripping (cyanide-based) and then the recovery of gold by the electrometallurgical route. First, the amount of gold was determined. Then, alternative leaching agents were tested under different concentrations and time. A cyanide-based solution was also tested to compare the results. The results showed that the content of gold varied from 142 to 700 g/ton. The cyanide-based solution was able to extract 88% of the gold, while sodium and ammonium thiosulfate extracted 70 and 75% of the gold, respectively. The electrowinning tests showed a 94% recovery of the gold present in thiosulfate solutions.

Currently, the recovery of materials from secondary sources is increasingly necessary because of the scarcity of materials. Significant amounts of rare earth elements (REE) are found in permanent neodymium-iron-boron (NdFeB) magnets, used in various electrical and electronic equipments, such as mobile phones. However, the estimated recycling rate for REEs is only 1%. Hydrometallurgical routes are the most commonly used for REE recovery from secondary sources. This route usually uses inorganic acids, which are expensive and toxic. Thus, in this work the leaching efficiency of organic acids (acetic and citric) in leaching the REE (neodymium and praseodymium) present in magnets of obsolete or defective mobile phones was evaluated. Different concentrations of acids, solid/liquid relations, times and leaching techniques (microwave, ultrasound and conventional) are also evaluated. The results indicate that acetic and citric acids have the potential to leach Nd and Pr. Microwave leaching was the most effective method, compared to ultrasound and conventional methods. In microwaves, citric acid at 0.5 M (ratio s/l 1/100) leached 57% of Nd and 58% of Pr. Acetic acid at 0.5 M (s/l ratio—1/100) leached 48% of Nd and 65% of Pr, in 15 min. Furthermore, both citric acid and acetic acid also leached high percentages of iron (51% and 72%, respectively).

Electronic scrap is part of a universally wide range of obsolete, defective, or used materials that need to be disposed of or recycled in an ecologically friendly manner. The present study focused on the polymers present in mobile phone scrap. In mobile phones, polymers are found in frames and in printed circuit boards (PCBs). The frames are mainly made of polymers whereas PCBs use a variety of material (polymers, ceramics, and metals) which makes recycling more difficult. As a first step, mobile phones were collected, separated by manufacturer/model, and weighed, and the principal polymer types identified. The frames and PCBs were processed separately. The metals in PCBs were separated out by an electrostatic separation process. The resulting polymeric material was identified and mixed with the polymers of frames to fabricate the samples. Two types of samples were made: one with polymeric frames, and the other with a mixture of frames and polymeric fraction from the PCBs. Both kinds of sample were fabricated by injection moulding. The samples were evaluated by mechanical tests (tensile, impact, and hardness) to verify the feasibility of recycling the polymers present in mobile phone scrap. The results demonstrated the technical viability of recovering polymers using mechanical processing followed by an injection process.