State-of-the-art in the studies of sodium-ion batteries is discussed in comparison with their deeper developed lithium-ion analogs. The principal problem hindering the development of competitive...

The performance of sodium-ion batteries largely depends on the presence and properties of passive films formed on the electrode/electrolyte interfaces. Passive films on negative electrodes inevitably result from the reduction in electrolyte components (solvent and salt anion). They have the properties of a solid electrolyte with sodium ion conductivity and are insulators in terms of electronic conductivity. Usually, they are called SEI—solid electrolyte interphase. The formation of SEI is associated with the consumption of a certain charge, which is an irreversible capacity. Passive films on the surface of positive electrodes (CEI—cathode electrolyte interphase) arise as a result of electrolyte oxidation. The present review summarizes the literature of the recent 15 years concerning the effects of electrode nature (hard carbon, other carbon materials, various metals, oxides, chalcogenides, etc.), electrolyte composition, and other factors on composition and properties of SEIs in sodium-ion batteries. Literary data on CEIs are reviewed as well, although their volume is inferior to that of data on SEIs.

The possibilities of manufacturing batteries with Nafion 117 membranes in the Na⁺-form intercalated by mixtures of non-aqueous organic solvents used both as an electrolyte, separator, and binder were investigated. Electrochemical stability of various organic solvent mixtures based on N,N-dimethylacetamide, ethylene carbonate, propylene carbonate, and tetrahydrofuran were characterized. It was shown that a sodium battery based on a Nafion-Na membrane intercalated by mixture of ethylene carbonate and propylene carbonate with a Na₃V_1.9Fe_0.1(PO₄)₃/C positive electrode is characterized by a discharge capacity of ≈110 mAh·g⁻¹ (current density of 10 mA·g⁻¹) at room temperature and shows the ability to cycle without degradation during 20 cycles. Batteries with Nafion membrane electrolytes, containing N,N-dimethylacetamide, were characterized using capacity fading during cycling, which is due to the interaction of N,N-dimethylacetamide and a negative sodium electrode.