The application of pultruded fiber reinforced polymer (FRP) composites in civil engineering is increasing as a high-performance structural element or reinforcing material for rehabilitation purposes. The advantageous aspects of the pultrusion production technique and the weaknesses arising from the 0° fiber orientation in the drawing direction should be considered. In this direction, it is thought that the structural performance of the profiles produced by the pultrusion technique can be increased with 90° windings by using different fiber types. This paper presents experimental studies on the effect of FRP composite wrapping on the flexure performance of reinforced concrete (RC) filled pultruded glass-FRP (GFRP) profile hybrid beams with damage analysis. The hybrid beams are wrapped fully and partially with Glass fiber reinforced polymer (GFRP) and carbon fiber reinforced polymer (CFRP) composites. Hybrid beam specimens with 0° to 90° fiber orientations were tested under three- and four-point bending loads. Based on the experimental load–displacement relationship results, initial stiffness, ductility, and energy dissipation capacity were compared. The experimental findings revealed that the maximum load-carrying capacities of beams produced with pultrude profiles increased by 24% with glass wrapping and 64.4% with carbon wrapping due to the change in the damages. A detailed damage analysis is provided. Similarly, significant increases were observed in structural performance ratios such as initial stiffness and ductility ratio.

The aim of this article was to investigate the effect of carbon nanotubes (CNTs) on the buckling behavior of fiber-reinforced polymer (FRP) composites. The materials used included three layers: carbon-fiber-reinforced polymer (CFRP), epoxy and CNTs. A set of mechanical tests, such as compression and buckling tests, was performed, and also analytical solutions were developed. Damage analysis was also carried out by controlling the damage initiation and crack progression on the composite samples. Experimental results revealed that using 0.3% with CNT additives enhanced the buckling performance of the composite. Finally, the average load-carrying capacity for the clamped–clamped boundary condition was 268% higher in the CNT samples and 282% higher in the NEAT samples compared to the simple–simple condition.

Pultruded fiber-reinforced polymer (PFRP) profiles have started to find widespread use in the structure industry. The position of the web openings on these elements, which are especially exposed to axial pressure force, causes a change in the behavior. In this study, a total of 21 pultruded box profiles were tested under vertical loads and some of them were strengthened with carbon-FRP (CFRP) and glass-FRP (GFRP). The location, number and reinforcement type of the web openings on the profiles were taken into account as parameters. As a result of the axial test, it was understood that when a hole with a certain diameter is to be drilled on the profile, its position and number are very important. The height-centered openings in the middle of the web had the least effect on the reduction in the load-carrying capacity and the stability of the profile. In addition, it has been determined that the web openings away from the center and especially the eccentric opening significantly reduces the load carrying capacity. Furthermore, when double holes were drilled close to each other, a significant decrease in the capacity was observed and strengthening had the least effect on these specimens. It was also determined that the specimens reinforced with carbon FRP contribute more to the load-carrying capacity than GFRP.

Web openings often need to be created in structural elements for the passage of utility ducts and/or pipes. Such web openings reduce the cross-sectional area of the structural element in the affected region, leading to a decrease in its load-carrying capacity and stiffness. This paper experimentally studies the effect of web openings on the response of pultruded fiber-reinforced polymer (PFRP) composite profiles under compressive loads. A number of specimens have been processed to examine the behavior of PFRP profiles strengthened with one or more web openings. The effects of the size of the web opening and the FRP-strengthening scheme on the structural performance of PFRP profiles with FRP-strengthened web openings have been thoroughly analyzed and discussed. The decrease in load-carrying capacity of un-strengthened specimens varies between 7.9% and 66.4%, depending on the diameter of the web holes. It is observed that the diameter of the hole and the type of CFRP- or GFRP-strengthening method applied are very important parameters. All CFRP- and GFRP-strengthening alternatives were successful in the PFRP profiles, with diameter-to-width (D/W) ratios between 0.29 and 0.68. In addition, the load-carrying capacity after reinforcements made with CFRP and GFRP increased by 3.1–30.2% and 1.7–19.7%, respectively. Therefore, the pultruded profiles with openings are able to compensate for the reduction in load-carrying capacity due to holes, up to a D/W ratio of 0.32. The capacity significantly drops after a D/W ratio of 0.32. Moreover, the pultruded profile with CFRP wrapping is more likely to improve the load-carrying capacity compared to other wrappings. As a result, CFRP are recommended as preferred composite materials for strengthening alternatives.