To explore the applicability of steel slag porous asphalt mixture, the interaction capability and microscopic interfacial mechanism between asphalt-binder and steel slag aggregate-filler were investigated in this laboratory study. These objectives were accomplished by comparing and analyzing the differences between steel slag and basalt aggregates in interacting with the asphalt-binder. The study methodology involved preparing basalt and steel slag asphalt mortar to evaluate the penetration, ductility, softening point, toughness, and tenacity. Thereafter, the interaction capability between the asphalt-binder and aggregates was characterized using the interaction parameters of the asphalt mortar obtained from dynamic shear rheometer (DSR) testing. For studying the functional groups and chemical bonding of the asphalt mortar, the Fourier Transform infrared (FTIR) spectrometer was used, whilst the interfacial bonding between the asphalt-binder and aggregates was analyzed using the scanning electron microscope (SEM). The corresponding test results indicated that the physical and rheological properties of the two asphalt mortars were similar. However, whilst the FTIR analysis indicated domination through chemical reactions, the interaction capability and interfacial bonding between the asphalt-binder and steel slag aggregates exhibited superiority over that between the asphalt-binder and basalt aggregates, with pronounced adsorption peaks appearing in the steel slag asphalt mortar spectrum. On the other hand, the SEM test revealed that, compared with the basalt, the micro-interfacial phases between the steel slag and asphalt-binder were more continuous and uniform, which could potentially enhance the interfacial bond strength between the asphalt-binder and aggregates (filler).

Asphalt binder is a complex mixture of dark brown polymers composed of hydrocarbons with generally poor fire resistance. To improve its flame retardancy when used in tunnel asphalt pavements, a new inorganic flame-retardant filler (FR) containing magnesium hydroxide, aluminum hydroxide, inorganic phosphate, and melamine salt was explored. Thereafter, limiting oxygen index (LOI) and smoke suppression tests for the flame-retarded asphalt binder (FRA) mastics mixed with FR and styrene-butadiene-styrene (SBS) copolymer asphalt binder were conducted. Thermogravimetric (TG) and differential scanning calorimetry (DSC) curves for the FRA were correspondingly generated. Based on the TG data, the reaction function g(α), apparent activation energy E_a, and pre-exponential factor A were quantitatively evaluated using kinetic analysis. In addition, a Fourier transform infrared spectrometry (FTIR) test was utilized to assess the effects of the presence of FR on the chemical composition of the asphalt binder. Dynamic shear rheometer (DSR) tests were also performed to evaluate the rheological behavior of FRA. Results show that the presence of the FR significantly reduced the LOI and improved the smoke suppression during combustion of the asphalt binder mastics. The presence of FR was found to increase the E_a and the complexity of the combustion reaction, thereby improving the flame retardancy of the asphalt binder. FTIR analysis indicated that the presence of FR did not induce any strong chemical reactions to significantly impact or alter the functional groups of the asphalt binder. Furthermore, it was also observed that the rutting parameter and critical failure temperature of FRA increased with the addition of FR due to the stiffening effect of the solid FR particles.