To explore the applicability of steel slag porous asphalt mixture, the interaction capability and microscopic interfacial mechanism between asphalt-binder and steel slag aggregate-filler were investigated in this laboratory study. These objectives were accomplished by comparing and analyzing the differences between steel slag and basalt aggregates in interacting with the asphalt-binder. The study methodology involved preparing basalt and steel slag asphalt mortar to evaluate the penetration, ductility, softening point, toughness, and tenacity. Thereafter, the interaction capability between the asphalt-binder and aggregates was characterized using the interaction parameters of the asphalt mortar obtained from dynamic shear rheometer (DSR) testing. For studying the functional groups and chemical bonding of the asphalt mortar, the Fourier Transform infrared (FTIR) spectrometer was used, whilst the interfacial bonding between the asphalt-binder and aggregates was analyzed using the scanning electron microscope (SEM). The corresponding test results indicated that the physical and rheological properties of the two asphalt mortars were similar. However, whilst the FTIR analysis indicated domination through chemical reactions, the interaction capability and interfacial bonding between the asphalt-binder and steel slag aggregates exhibited superiority over that between the asphalt-binder and basalt aggregates, with pronounced adsorption peaks appearing in the steel slag asphalt mortar spectrum. On the other hand, the SEM test revealed that, compared with the basalt, the micro-interfacial phases between the steel slag and asphalt-binder were more continuous and uniform, which could potentially enhance the interfacial bond strength between the asphalt-binder and aggregates (filler).

To investigate the influence of multiple cycles of aging and rejuvenation on the rheological, chemical, and morphological properties of styrene–butadiene–styrene (SBS)-modified asphalt-binders, the asphalt-binders were aged using two laboratory simulation methods, namely a rolling thin film oven (RTFO) test for short-term aging and pressure aging vessel (PAV) for long-term aging. The asphalt-binders were then rejuvenated with three types of rejuvenators (Type I, II, and III) with different dosages (i.e., 6%, 10%, and 14% for the first, second, and third rejuvenation, respectively). A dynamic shear rheometer (DSR) was then used to analyze the effect of rejuvenators on the rheological properties of all the asphalt-binders. The changes in the functional groups and microscopic morphology in the process of multiple aging and rejuvenation cycles were studied using Fourier transform infrared (FTIR) and atomic force microscopy (AFM). The results indicated that the three rejuvenators could soften the stiffness and restore the microstructures of the aged asphalt-binders in the process of repeated aging and rejuvenation from DSR and AFM testing. Considering the rutting and fatigue properties, the Type I rejuvenator exhibited the potential to achieve the desired rejuvenation effects under multiple rejuvenation cycles. During the multiple aging and rejuvenation cycles, the aging resistance of SBSMA decreased gradually from the FTIR results. This inherently limited the number of repeated rejuvenation cycles. This research is conducive to promoting the application of repeated penetrating rejuvenation.

A steel slag porous asphalt (SSPA) mixture, as the surfacing layer of permeable asphalt pavements, not only ensures the pavement surface drainage and noise reduction functions, but also improves the comprehensive utilization of steel slag resources and the inherent protection of the ecological environment. However, compared with ordinary asphalt mixtures, SSPA is more susceptible to water damage, such as scouring and frost swelling caused by external rainwater intrusion, resulting in the deterioration of the pavement performance. Therefore, it is of good practical imperative to study the water stability and moisture damage mechanism of SSPAs. In this study, the water stability of SSPA, that was subjected to a series of time–temperature H₂O-immersion schemes, was investigated using the pull-out and H₂O-immersion Marshall tests, whilst the microscopic mechanism of moisture damage was studied using the scanning electron microscopy (SEM), Fourier infrared spectroscopy (FTIR), and X-ray diffraction (XRD) tests. The corresponding results showed that: (a) with the increase in the H₂O immersion time, the water stability of SSPA first increased and then decreased; and (b) the water stability of SSPA was strong under medium-temperature H₂O-immersion or short-term high-temperature H₂O-immersion. SEM, on the other hand, showed that the transition zone spacing was closely related to the chemical adhesion mechanism between the asphalt and steel slag aggregate. Additionally, the FTIR analysis further showed that the steel slag asphalt mastic spectra had new absorption peaks at 3200~3750 cm⁻¹, inherently indicating the existence of chemical bonding between the asphalt and steel slag, with the XRD results showing that CaSO₄·2H₂O had a beneficial effect on the water stability of SSPA.