Recent studies have indicated a great demand to optimize the biocompatibility properties of pure Zn as an implant material. For this purpose, CaZn₂(PO₄)₂·2H₂O (CaZnP) was prepared using hydrothermal treatment (HT) combined with micro-arc oxidation (MAO) on pure Zn substrate to generate biodegradable implants. The polarization test and electrochemical impedance spectroscopy indicated that the MAO1−HT coating could modulate the corrosion behavior of MAO1 by filling the crevice between the coating and the substrate. Immersion test evaluation revealed that the osteogenic properties of MAO1−HT coating were better than that of pure Zn substrate, as evidenced by the molar ratio of Ca and P, which increased after soaking in simulated body fluid (SBF) for up to 10 days. In addition, L-929 cells cultured in the 100%, 50%, and 25% extracts of MAO1−HT coated samples exhibited excellent cytocompatibility. Meanwhile, cell adhesion was promoted on the surface with high roughness generated during MAO and HT processes. In summary, the calcified coatings improved biocompatibility and adjusted the degradation rates of pure Zn, broadening the application of Zn alloys.

Aluminum foam that is lightweight with high specific strength, high energy absorption and other characteristics can be used in aerospace, transportation, machinery manufacturing and other fields. The PCM method is usually used to prepare closed-cell aluminum foams. The microsized aluminum foams made by this process can solve the non-uniform pore structures caused by liquid drainage during the foaming process of large aluminum foams. The surface morphology and internal pore structure of microsized aluminum foams are affected by the quality of the precursor used for foaming. In this paper, foamable precursors were obtained via either hot rolling or hot extrusion and subsequently foamed. By analyzing the micromorphology and foaming process of the precursor, the influence of the technological method on the macroscopic pore structure of the final aluminum foam was studied. The results show that the aluminum powder particles in the precursor prepared with the hot rolling method had metallurgical bonding, and the outer surface was dense, with almost no porosity and holes in the interior. The microsized aluminum foam obtained after foaming was smooth in appearance, and the internal pore structure was round and uniform. The reason is that during the foaming process of microsize aluminum foam, the foaming agent was evenly distributed in the precursor of the hot rolling process because of its compact structure. During the foaming process, the decomposed gas of the foaming agent will not escape, and the evenly distributed foaming agent tends to nucleate in situ. In the process of rapid foaming, the pressure in the bubble is enough to resist the liquid drainage phenomenon caused by gravity, and the growth direction of the gas core is isotropic, which promotes the foam structure to be more rounded and uniform.

The space holder method, a kind of powder metallurgy method which can avoid the process of melting metal to prepare metal foams, has particular significance in solving the difficulty of preparing metal foams with high melting points. In this paper, Na₂S₂O₃·5H₂O, a novel space holder, was used to prepare aluminium foam and copper foam, which were then used to test the heat dissipation performance of the metal foams. We first prepared two kinds of cell structures for (spherical cell and composite cells) aluminium and copper foam, then, we compared the performances of their heat dissipation, and it was found that both the spherical cell metal foam and composite cell metal foam promoted heat dissipation in the environment of natural convection, and the difference between them was not apparent. In the environment of forced convection, the composite porous metal showed a better heat dissipation performance.